Abstract:
|
SIMA was adopted to make semi-solid billet.7A09 cast ingot of Ф33 mm×15 mm was used to make billet by direct extrusion and isothermal treatment.The billet was observed by metallographic method in order to determine the parameters for making the semi-solid billet.The main factors in this experiment were extrusion ratio,isothermal temperature and holding time.The results show that the preferred values are extrusion ratio of 7,mould temperature of 300 ℃,cast condition sample's heating temperature of 450 ℃ and holding for 30 min and lower extrusion velocity in the process of billet pretreatment.In the process of isothermal treatment,heating temperature of 617 ℃ and holding for 19 min can acquire perfect semi-solid microstructure.
|
Funds:
|
|
AuthorIntro:
|
|
Reference:
|
[1]褚祥治,齐铁力,刘芳,等.半固态合金成形技术综述[J].唐山学院学报,2005,18(4):107-110.
[2]胥锴,吴子平,刘萍.半固态金属成形技术及应用[J].冶金丛刊,2005,160(6):30-33,47.
[3]Luo Shoujing,Tian Wenxing,Zhang Guang-an.Structuralevolution of LC4 alloy in making thixotropic billet by SIMAmethod[J].Trans.Nonferrous Met.Soc.China,2001,11(8):547-551.
[4]姜巨福,彭秋才,单巍巍,等.新SIMA法制备AZ91D半固态坯[J].特种铸造及有色合金,2005,25(12):740-743.
[5]江海涛,黄维超,卢雅琳,等.半固态LY11铝合金的组织演变研究[J].稀有金属材料与工程,2004,33(8):869-872.
[6]江海涛,李淼泉.SIMA制备半固态LY11合金的工艺研究[J].锻压技术,2003,28(3):37-39.
[7]姚亮宇,袁森,王武孝,等.SIMA法处理AZ91D镁合金压缩形变及半固态等温组织的特征[J].中国有色金属学报,2004,14(4):660-664.
[8]赵祖德,罗守靖.半固态成形应用现状与未来[J].锻压技术,2006,31(6):1-3.
[9]武恭,姚良均.铝及铝合金材料手册[M].北京:科学出版社,1994.
|
Service:
|
【This site has not yet opened Download Service】【Add
Favorite】
|
|
|