热作模具钢高温销-盘磨损实验研究

英文标题：Experimental research on high temperature pin-disc wear for hot work die steel

分类号：TG376

出版年,卷(期):页码：2022,47(1):172-179

摘要：

为研究3种常用热作模具钢的高温硬度和在100和300 ℃温度条件下的磨损率、摩擦因数的变化规律，通过高温硬度实验和高温摩擦磨损实验获得了3种热作模具钢的硬度、摩擦因数、磨损率随温度的变化规律。结果表明：随着温度的升高，硬度逐渐下降，表面渗氮处理虽能够大幅度提高材料硬度，但渗氮处理后的硬度随着温度升高而下降的幅度更明显；300 ℃下，销-盘接触表面的变形抗力降低，材料与板材之间的摩擦因数小于100 ℃下的摩擦因数，同时300 ℃下销表面产生较厚的氧化层，其磨损率小于100 ℃下的磨损率；材料表面渗氮处理后在100 ℃下材料的耐磨性提高，但在300 ℃下磨损量反而增大。实验结果为模具材料的选择和模具耐磨性的提高提供了可靠的基础数据支撑。

In order to study the high temperature hardness of three commonly used hot work die steels and the change laws of wear rate and friction coefficient at 100 and 300 ℃, the laws for the hardness, friction coefficient and wear rate changing with temperature for three types of hot work die steels were obtained by high temperature hardness test and high temperature friction-wear test. The results show that the hardness gradually decreases with the increasing of temperature. Although the surface nitriding treatment greatly increases the hardness of the material, the hardness decreases more obviously with the increasing of temperature after nitriding treatment. At 300 ℃, the resistance to deformation of the pin-disk contact surface is reduced, and the friction coefficient between material and plate is less than that at 100 ℃. At the same time, the pin surface produces a thicker oxide layer at 300 ℃, and the wear rate is less than that at 100 ℃. The surface nitriding treatment of the material improves the wear resistance of the material at 100 ℃, but at 300 ℃, the wear amount increases instead. Thus, the test results provide reliable basic data support for the selection of mold materials and the improvement of mold wear resistance.

基金项目：

高品质热作模具钢研发与产业化（2020B010184002）

作者简介：张赛军（1978-），男，博士，副教授 E-mail：mesjzhang@scut.edu.cn

参考文献：

[1] 门超, 徐晓东. 支撑板冲压成形模具磨损分析及优化[J]. 锻压技术, 2020,45(3):131-136.

Men C, Xu X D. Wear analysis and optimization of stamping die for support plate[J]. Forging & Stamping Technology, 2020, 45(3):131-136.

[2] Archard J F. Contact and rubbing of flat surfaces[J]. Journal of Applied Physics, 1953, 24(8): 981-988.

[3] Stoehr T, Merklein M, Lechler J. Determination of frictional and thermal characteristics for hot stamping with respect to a numerical process design[A]. 1st International Conference on Hot Sheet Metal Forming of Highperformance Steel[C]. Kassel，2008.

[4] Carlsson P, Bexell U, Olsson M. Tribological performance of thin organic permanent coatings deposited on 55% AlZn coated steelInfluence of coating composition and thickness on friction and wear[J]. Wear, 2001, 251(1-12): 1075-1084.

[5] Groche P, Moeller N, Hoffmann H, et al. Influence of gliding speed and contact pressure on the wear of forming tools[J]. Wear, 2011, 271(9-10): 2570-2578.

[6] Hardell J, Prakash B. Hightemperature friction and wear behaviour of different tool steels during sliding against AlSicoated highstrength steel[J]. Tribology International, 2008, 41(7): 663-671.

[7] Borsetto F, Ghiotti A, Bruschi S. Investigation of the high strength steel AlSi coating during hot stamping operations[A]. Sheet Metal[C]. Italy, 2009.

[8] Wang W, Zheng X, Hua M, et al. Influence of surface modification on galling resistance of DC53 tool steel against galvanized advanced high strength steel sheet[J]. Wear, 2016, 360: 1-13.

[9] Leite M V, Figueroa C A, Gallo S C, et al. Wear mechanisms and microstructure of pulsed plasma nitrided AISI H13 tool steel[J]. Wear, 2010, 269(5-6): 466-472.

[10]宋宇, 张丰收,皇涛,等.基于高温磨损的H13热作模具钢磨损规律和模型研究[J].塑性工程学报,2018,25(4):187-193.

Song Y, Zhang F S, Huang T, et al. Study on wear and model of H13 hot working die steel based on hightemperature wear[J]. Journal of Plasticity Engineering, 2018, 25(4):187-193.

[11]陈杰. H13钢表面磨损行为的数值模拟研究及模具寿命预测[D]. 长春：吉林大学, 2015.

Chen J. Numerical Simulation Study of Surface Wear Behavior of H13 Steel and Die Life Prediction of the Mould Life[D]. Changchun: Jilin University, 2015.

[12]刘义. 超高强钢热成形摩擦磨损及其对成形性能的影响[D]. 南京：江苏大学, 2020.

Liu Y. Friction and Wear of Ultrahigh Strength Steel During Hot Forming and Its Effects on Forming Properties[D]. Nanjing: Jiangsu University, 2020.

[13]铁争鸣. 基于响应面法的幅板冲压成形模具磨损[J].锻压技术,2021,46(5):174-178.

Tie Z M. Wear of stamping mould for shield based on response surface method[J]. Forging & Stamping Technology, 2021, 46(5):174-178.

[14]李爽. 新型热冲压模具钢组织与高温摩擦磨损机理研究[D]. 上海：上海大学,2017.

Li S. The Study on Microstructure and High Temperature Friction and Wear Mechanism of New Type Hot Stamping Die Steel[D]. Shanghai: Shanghai University, 2017.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】