锻压技术

国内外DC53模具钢组织及力学性能对比研究

英文标题：Comparative research on microstructure and mechanical properties of DC53 die steel made in China and abroad

单位：1.天津职业技术师范大学 2. 国家模具产品质量监督检验中心 3. 广东省东莞市质量监督检测中心

分类号：TG142.45

出版年,卷(期):页码：2021,46(10):218-224

摘要：

通过化学成分、金相、SEM、EDS、XRD、硬度和韧性等实验，对国内外DC53冷作模具钢的显微组织和力学性能进行对比。结果表明：国内外DC53冷作模具钢的原材料化学成分无明显差异，退火态的进口DC53模具钢拥有比国产DC53模具钢更好的洁净度和更为均匀的碳化物分布，进口与国产DC53模具钢的退火硬度分别为240和255 HBS。经相同的标准热处理（淬火+回火）后，分别测得进口与国产DC53模具钢中含有4.56%和3.23%的残余奥氏体；进口DC53模具钢热处理后的硬度和韧性测试结果分别为61.9 HRC和11.6 J；国产DC53模具钢热处理后的硬度和韧性测试结果分别为61.6 HRC和7.6 J。经热处理后两种钢的硬度相当，但进口DC53模具钢的韧性更为优异。

The microstructure and mechanical properties of DC53 cold working die steels in China and abroad were compared by experiments of chemical composition, metallography, SEM, EDS, XRD, hardness and toughness. The results show that there is no significant difference in the chemical compositions of raw materials for DC53 cold working die steels in China and abroad, imported DC53 die steel in annealed state has better cleanliness and more uniform carbide distribution than domestic DC53 die steel, and the annealed hardness of imported and domestic DC53 die steels are 240 and 255 HBS, respectively. After the same standard heat treatment (quenching+tempering), 4.56% and 3.23% retained austenite are measured in imported and domestic DC53 die steels respectively, and the hardness and toughness test results of imported and domestic DC53 die steels after heat treatment are 61.9 HRC and 11.6 J, 61.6 HRC and 7.6 J, respectively. Thus, their hardness after heat treatment is comparable, but the toughness of imported DC53 die steel is more excellent.

基金项目：

重要工业原材料（模具钢材产品）质量国际比对研究

作者简介：邱华兴（1997-），男，硕士研究生 E-mail：huaxingq@126.com 通信作者：蔡玉俊（1970-），男，博士，教授 E-mail：cyjal@126.com

参考文献：

[1]邱凌, 吴晓春. 国内外冷作模具钢发展概述[J]. 模具制造, 2017, 17(11): 89-96.

Qiu L, Wu X C. Overview of development of cold working die steel at home and abroad [J]. Die Manufacturing, 2017, 17(11): 89-96.

[2]吴茜, 刘斌. 模具材料研究与应用现状及发展趋势[J]. 模具工业, 2017, 43(3): 1-7，20.

Wu Q, Liu B. Research and application status and development trend of mold materials [J]. Mold Industry, 2017, 43(3): 1-7，20.

[3]GB/T 11170—2008, 不锈钢多元素含量的测定火花放电原子发射光谱法(常规法) [S].

GB/T 11170—2008, Stainless steel—Determination of multi-element contents—Spark discharge atomic emission spectrometric method (Routine method) [S].

[4]GB/T 10561—2005，钢中非金属夹杂物含量的测定标准评级图显微检验法[S].

GB/T 10561—2005，Steel—Determination of content of nonmetallic inclusions—Micrographic method using standards diagrams [S].

[5]祝家祺, 谭谆礼, 张敏, 等. 钒和铬对贝氏体车轮钢回火组织与性能的影响[J]. 稀有金属, 2020, 44(9): 957-966.

Zhu J Q, Tan Z L, Zhang M, et al. Microstructure and mechanical properties of tempered bainitic railway wheel steels with addition of V and Cr [J]. Chinese Journal of Rare Metals, 2020, 44(9): 957-966.

[6]王泽, 王婷婷, 金东浩, 等. 高合金钢冷轧工作辊锻造过程数值模拟[J]. 锻压技术, 2020, 45(1): 22-29.

Wang Z, Wang T T, Jin D H, et al. Numerical simulation of forging process for high alloy steel cold work roller [J]. Forging & Stamping Technology, 2020, 45(1): 22-29.

[7]宗男夫, 张慧, 刘洋, 等. 连铸轴承钢偏析和凝固组织缺陷的成因及其危害[J]. 轴承, 2018, (6): 62-67.

Zong N F, Zhang H, Liu Y, et al. Causes and hazards of segregation and solidification structure defects in continuous casting bearing steel [J]. Bearing, 2018，(6): 62-67.

[8]GB/T 14979—94, 钢的共晶碳化物不均匀度评定法[S].

GB/T 14979—94, Eutectic carbide of steel—Micrographic method using standard diagrams[S].

[9]何仙灵, 杨庚蔚, 毛新平, 等. CSP热轧50CrV4带钢普通球化退火工艺[J]. 钢铁研究学报, 2017, 29(10): 831-837.

He X L, Yang G W, Mao X P, et al. Common spheroidizing annealing process of CSP hot rolled 50CrV4 strip [J]. Acta Iron and Steel Research, 2017, 29(10): 831-837.

[10]崔敏超, 赵升吨, 陈超, 等. 42CrMo钢中温成形性研究[J]. 热加工工艺, 2017, 46(9): 1-6.

Cui M C, Zhao S D, Chen C, et al. Study on medium temperature formability of 42CrMo steel [J]. Hot Working Technology, 2017, 46(9): 1-6.

[11]王定祥. 耐磨钢铁材料Ms点控温淬火法[J]. 铸造设备与工艺, 2017，(1): 49-54，66.

Wang D X. MS point temperature controlled quenching method for wear resistant steel materials [J]. Casting Equipment and Technology, 2017，(1): 49-54，66.

[12]李冬丽. Si含量变化对Cr8Mo2SiV钢组织性能影响的研究[D]. 昆明：昆明理工大学, 2010.

Li D L. Effect of Si Content on Microstructure and Properties of Cr8Mo2SiV Steel [D]. Kunming：Kunming University of Science and Technology, 2010.

[13]FB Pickering. Physical Metallurgy and the Design of Steels[M]. Applied Science Publishers, 1978.

[14]Lee K B, Kwon H. Fracture behavior of secondary hardening steels[J]. Scripta Metallurgica et Materialia, 1992, 27(10): 1355-1360.

[15]王大鹏, 穆云超, 成晓哲, 等. 原料配比对放电等离子烧结钼碳化物的影响[J]. 粉末冶金技术, 2018, 36(1): 31-35.

Wang D P, Mu Y C, Cheng X Z, et al. Effect of raw material ratio on spark plasma sintering of molybdenum carbide [J]. Powder Metallurgy Technology, 2018,36(1): 31-35.

[16]吕昭平, 雷智锋, 黄海龙, 等. 高熵合金的变形行为及强韧化[J]. 金属学报, 2018, 54(11): 1553-1566.

Lyu Z P, Lei Z F, Huang H L, et al. Deformation behavior and strengthening and toughening of high entropy alloys [J]. Acta metallurica Sinica, 2018, 54(11): 1553-1566.

[17]王晶, 黄少文, 刘金超, 等. 板材拉伸冲击试样断口识别及分析[J]. 物理测试, 2016, 34(1): 29-35.

Wang J, Huang S W, Liu J C, et al. Fracture identification and analysis of plate tensile impact specimen [J]. Physical Test, 2016, 34(1): 29-35.

[18]贾克明, 王丽凤, 张世勇, 等. BGA单板结构与板级结构焊点剪切力学行为分析[J]. 焊接学报, 2018, 39(3): 94-98，133.

Jia K M, Wang L F, Zhang S Y, et al. Shear mechanical behavior analysis of BGA single plate structure and plate level structure [J]. Acta Welding Sinica, 2018, 39(3): 94-98，133.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】