以厚度为0.8 mm的DP1180先进高强度钢板料拉深成形为例，利用HIF-60小松伺服压力机的拉深成形系统速度和压边力可调的特点，对其进行拉深极限测定实验。通过室温下的拉深实验得到了该板料在室温下的极限拉深直径为Ф54.50 mm，极限拉深比LDR为2.07。通过只改变单一变量，进一步研究了在不同的压边力、冲压速度以及润滑条件下的极限拉深直径，以及对应的各工艺参数下的LDR值。通过正交实验来设计优化方案，通过方差分析得到了影响先进高强度钢DP1180拉深工艺的因素的主次顺序为：压边力＞润滑＞冲压速度，通过极差分析得到了最优参数组合为：压边力为10 kN、采用油脂润滑、冲压速度为5 mm·s-1。对优化后的参数组合进行验证，实验表明：优化后的拉深成形件成形效果良好，无明显缺陷，且室温下的极限拉深直径增大为Ф55.75 mm，极限拉深比增大为2.12。
|
|
For the deep drawing of advanced high-strength steel DP1180 sheet material with 0.8 mm, the drawing limit measurement experiment was carried out by adjusting speed and blank holder force in the deep drawing system of servo press Komatsu HIF-60, and the limit drawing diameter of Ф54.50 mm and the limit drawing ratio of 2.07 for this sheet material were obtained by the drawing experiment at room temperature. Then, the limit drawing diameter under different blank holder forces, stamping speeds and lubrication conditions, and the LDR values under the corresponding process parameters were further studied by changing only a single variable, and the optimization scheme was designed by the orthogonal experiment. Furthermore, through the variance analysis, the primary and secondary order of influencing factors affecting the deep drawing process of advanced high-strength steel was obtained as follows: the blank holder force, the lubrication, the stamping speed, and the optimal combination of parameters was obtained with the blank holder force of 10 kN, the grease lubrication, and the stamping speed of 5 mm·s-1 by the range analysis. The verification experiment of the optimized parameter combination shows that the optimized deep drawing part has good forming effect without obvious defects, and the limit drawing diameter and the limit drawing ratio at room temperature is increased to Ф55.75 mm and 2.12, respectively.
|
|
基金项目：
|
|
国家自然科学基金资助项目（51805315）
|
|
作者简介：
|
|
作者简介：宣守强(1994-), 男，硕士研究生，E-mail：XSQ19941003@163.com；通信作者：邓沛然(1970-)，男，博士，讲师，E-mail：peirandeng@126.com
|
|
参考文献：
|
[1]马廷涛, 庄厚川,金科,等.高强钢材料车身轻量化研究[J].汽车工艺与材料,2019,(5):1-5,11.
Ma T T, Zhuang H C, Jin K, et al. A study on lightweight of high strength steel body [J]. Automobile Technology & Material, 2019, (5): 1-5,11.
[2]Sun S D, Guo B, Shan D B, et al. Research on elevated temperature deformation behavior of Ti-6Al-4V sheets[J].Rare Metals, 2009, 28(6):550-553.
[3]孔政, 张杰,李洪波,等.摩擦系数对DP780钢拉深成形极限的影响[J].塑性工程学报,2018,25(2):252-259.
Kong Z, Zhang J, Li H B, et al. Effects of friction coefficient on the deep-drawing forming limit of dual-phase steel [J]. Journal of Plastic Engineering, 2018,25(2):252-259.
[4]崔振楠, 林利,朱国明,等.DP590/DP780高强钢管液压成形的性能[J].工程科学学报,2020,42(2):233-241.
Cui Z N, Lin L, Zhu G M, et al. Hydroforming performance of DP590/DP780 high-strength steel tube [J]. Chinese Journal of Engineering, 2020,42(2):233-241.
[5]Sandeep Pandre, Prathamesh Takalkar, Nitin Kotkunde, et al. Influence of temperatures and strain rates on tensile deformation behaviour of DP590 steel[J]. Materials Today: Proceedings, 2019, 18(7): 2603-2610.
[6]GB/T 15825.1—2008, 金属薄板成形性能与试验方法第1部分：成形性能和指标[S].
GB/T 15825.1—2008, Sheet metal formability and test methods—Part 1: Formability and indexes [S].
[7]翟晓晨, 董金善,王建军,等.基于ANSYS的平板封头矩形大开孔优化设计[J]. 轻工机械, 2017, 35(5): 81-85.
Zhai X C, Dong J S, Wang J J, et al. Optimization design of rectangular large opening in flat head based on ANSYS [J]. Light Industry Machinery, 2017, 35(5):81-85.
[8]赵长财, 曹秒艳,肖宏,等.镁合金板材的固体颗粒介质拉深工艺参数[J].中国有色金属学报,2012,22(4):991-999.
Zhao C C, Cao S Y, Xiao H, et al. Solid granular medium drawing process parameters of magnesium alloy sheet [J].Chinese Journal of Nonferrous Metals,2012,22(4):991-999.
[9]高贵杰, 雷君相.矩盒形件压边拉深工艺[J].塑性工程学报,2014,21(5):30-34.
Gao G J, Lei J X. Research on stamping of rectangular box using binder [J]. Journal of Plastic Engineering, 2014, 21(5):30-34.
[10]Naka T, Yoshida F. Deep drawability of type 5083 aluminium-magnesium alloy sheet under various conditions of temperature an forming speed[J]. Journal of Materials Processing Technology, 1999, 89-90:19-23.
[11]陈吉清, 王玉超,兰凤崇. 基于正交试验的汽车覆盖件冲压工艺参数优化[J]. 计算机集成制造系统, 2007, 13(12):2433-2440.
Chen J Q, Wang Y C, Lan F C. Optimization for stamping process parameters of automotive body parts based on orthogonal experiments [J].Computer Integrated Manufacturing Systems,2007,13(12):2433-2440
[12]周旭, 杨平,毛卫平,等.基于正交试验法的COB-LED散热器优化设计[J].轻工机械,2018,36(4):76-80.
Zhou X, Yang P, Mao W P, et al. Optimization design of COB-LED radiator based on orthogonal test [J].Light Industrial Machinery, 2018, 36(4):76-80.
[13]刘建鹏, 王震虎,林启权,等.基于正交试验的铝代钢冲压成形工艺参数优化[J].塑性工程学报,2018,25(5):110-116.
Liu J P, Wang Z H, Lin Q Q, et al. Optimization of stamping process parameters for aluminum instead of steel based on orthogonal experiment [J].] Journal of Plasticity Engineering,2018,25(5):110-116.
|
|
服务与反馈：
|
|
【本网站尚未开通全文下载服务】【加入收藏】
|
|
|
|