锻压技术

两厢车型顶盖尾部起皱研究及优化方案

英文标题：Research on wrinkle for hatchback car roof rear and its optimization scheme

作者：高双明

分类号：TG386

出版年,卷(期):页码：2021,46(2):76-81

摘要：

以实际生产中某MPV车型出现的顶盖尾部造型两位置的起皱案例为基础，通过对模具结构以及原有生产工艺进行分析，结合现场生产情况的跟踪调查，采用CAE软件对冲压件生产过程进行模拟，找出起皱产生的主要原因，并分别针对两位置的起皱原因制定顶盖尾部起皱优化工艺。在前工序加工过程中，会因工艺型面R角产生加工硬化;而在后工序整形中，该硬化部分形状不能恢复平整，导致出现型面起皱缺陷。通过消除加工硬化，提高零件装车匹配性及车身精度，避免顶盖在冲压成形过程中因起皱、叠料导致的凸、凹模型面磨损快，提高模具使用寿命。

For the wrinkling in two positions of an MPV car roof rear during the actual production, the main causes of wrinkles were obtained by analyzing the die structure and the original production process, combining with the tracking investigation of on-site production situation and simulating the production process of stamping parts by CAE software, and the optimization process of wrinkles in the roof rear was formulated according to the wrinkle causes of the two positions. In the process of previous process, the work hardening occurred at R angle of process surface, and in the subsequent process of shaping, the shape of hardened part could not be restored to flatness resulting in surface wrinkling defect. Thus, by eliminating work hardening, the matching of loading for parts and the accuracy of car body were improved to avoid the rapid wear of punch and die surfaces caused by wrinkling and stacking materials in stamping process of roof so as to improve the service life of die.

基金项目：

国家科技重大专项（2014ZX04002041）

高双明（1989-），男，学士，工程师，E-mail：1381033@163.com

参考文献：

[1]吕进，崔奎.汽车顶盖冲压常见问题及解决措施[J].模具技术，2015, (6): 45-48.
Lyu J, Cui K.The problems and solutions of automobile roof stamping process [J].Die and Mould Technology，2015, (6): 45-48.
[2]闫华军，王波，张双杰，等.铝合金地板梁拉延成形回弹分析及补偿[J].塑性工程学报，2020，27（2）：21-28.
Yan H J，Wang B，Zhang S J, et al.Springback analysis and compensation of drawing of aluminum alloy floor beam[J].Journal of Plasticity Engineering，2020，27（2）：21-28.
[3]郑金桥，黄勇，王义林，等.汽车覆盖件冲压工艺设计现状及发展趋势[J].塑性工程学报，2003，10(6)：9-14.
Zhen J Q, Huang Y, Wang Y L, et al.Present situation and prospects of stamping process planning for automobile panels[J].Journal of Plasticity Engineering, 2003，10(6)：9-14.
[4]韩小后，殷言春，朱取才.两厢轿车顶盖尾部冲压工艺优化设计[J].模具工业,2014, 40（5）:37-39.
Han X H,Yin Y C,Zhu Q C.Optimization design of stamping process for hatchback car roof cover end[J].Die & Mould Industry, 2014, 40（5）:37-39.
[5]王肖英，黄永生，刘迪祥,等.某卡车顶盖外板冲压工艺分析[J].模具制造, 2017, (3):15-18.
Wang X Y, Huang Y S, Liu D X, et al.Stamping process analysis of truck roofs plate[J].Die & Mould Manufacture, 2017, (3): 15-18.
[6]李骁,郑松林,张振华,等.汽车门内板冲压成形起皱研究[J].热加工工艺, 2014, 43(7):154-158.
Li X, Zheng S L, Zhang Z H, et al.Wrinkling research on auto inner door in sheet metal stamping forming[J].Hot Working Technology, 2014, 43(7):154-158.
[7]何锦艳，冯利君.顶盖外板面品问题解方法[J].模具制造, 2016, (7):6-8.
He J Y, Feng L J.Solution of the surface quality study for the roof outer [J].Die & Mould Manufacture,2016, (7):6-8.
[8]向小双.侧围外板冲压工艺分析[J].热加工工艺,2013，42(1)：78-84.
Xiang X S.Analysis of stamping process for side wall outer panel[J].Hot Working Technology, 2013，42(1)：78-84.
[9]陈武明，唐稳生，樊振林.大型薄板冲压件起皱破裂问题的解决[J].装备制造技术, 2010, (10)：159-167.
Chen W M, Tang W S, Fan Z L.The problem solution about wrinkle and rupture for large plate stamping[J].Equipment Manufactring Technology, 2010, (10)：159-167.
[10]高满银.基于抗凹理论对两厢汽车顶盖外板尾部波浪问题的分析[J].模具工业，2017,43(3):34-41.
Gao M Y.Analysis on the wave occurred on the rear of hatchback car roof panel based on the dent resistance theory [J].Die & Mould Industry, 2017,43(3):34-41.
[11]王良芬，李慧，高亮,等.侧围外板起皱问题分析及控制措施[J].模具工业，2017,43(10):28-31.
Wang L F, Li H, Gao L, et al.Analysis and control measurements of wrinkling for lateral outer panel [J].Die & Mould Industry, 2017,43(10):28-31.
[12]张学文，王冲，缑彦甫.基于CAE技术的顶盖外板结构改进及工艺验证[J].模具工业，2017,43(10):43-46.
Zhang X W, Wang C, Gou Y F.Structure improvement and technology verification of outer plate based on CAE technology [J].Die & Mould Industry, 2017,43(10):43-46.
[13]雷蕾，何晓聪，高爱凤，等.基于试验与数值模拟对比的钛合金压印接头研究[J].塑性工程学报，2019，26（3）:125-130.
Lei L, He X C, Gao A F, et al.Study on clinching joint of titanium alloy based on comparison of test and numerical simulation [J].Journal of Plasticity Engineering,2019，26（3）:125-130.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】