摘要：
|
|
设计了一种采用不同浇注系统的铝合金拉伸试样金属型模具，以减少铸件的缺陷、提升铸件的质量。利用ProCAST对铸造过程进行模拟，对拉伸试样充型凝固过程中的各物理场进行分析，预测其铸造缺陷和二次枝晶臂间距。确定优化模具的合理性后进行实验验证。实验结果表明：优化模具能够有效阻止前沿含有氧化薄膜的金属熔体进入型腔；优化模具的扇形流道，使充型过程平稳，避免型腔内出现卷气现象；试样能够实现顺序凝固，成功消除试样中的缩松、缩孔缺陷；优化模具试样的二次枝晶臂间距为33.2 μm，抗拉强度为215 N·mm-2，屈服强度为173 N·mm-2，断后伸长率为4.5%。优化后的模具能有效地减少拉伸试样中的铸造缺陷并减小二次枝晶臂间距，提升了拉伸试样的力学性能。
|
|
A metal mold of aluminum alloy tensile specimen with different pouring systems was designed to reduce the defects of casting part and improve the quality of casting part, and the casting process was simulated by software ProCAST. Then, the physical fields during the filling and solidification process of tensile samples were analyzed, and the casting defects and the secondary dendritic arm spacing were predicted. Furthermore, the rationality of the optimized mold was determined and verified by experiments. The results show that the optimized mold effectively prevents the metal liquid with oxide film in the front stage from entering the cavity, and the tapered runner in the optimized mold makes the filling process stable to avoid the phenomenon of gas filling in the cavity. In addition, the sample realizes solidified sequentially and successfully eliminates the shrinkage defect, the secondary dendrite arm spacing of specimen is 33.2 μm, the tensile strength is 215 N·mm-2, the yield strength is 173 N·mm-2, and the elongation after fracture is 4.5%. Thus, the optimized mold effectively reduces the casting defects in the tensile samples and the secondary dendrite arm spacing, and the mechanical properties of tensile specimens are improved.
|
|
基金项目：
|
|
|
|
作者简介：
|
|
王彦凤（1970-），女，硕士，副教授，E-mail：wyf70518@163.com
|
|
参考文献：
|
[1]孔维兵，胡心平，王洪飞，等. 铝镁合金金属型拉伸试样铸造工艺的优化[J]. 铸造技术，2016，37(1)：83-86.
Kong W B, Hu X P, Wang H F，et al. Casting process optimization of metal mold tensile specimen for aluminum magnesium alloy[J]. Foundry Technology, 2016，37(1):83-86.
[2]邱彬，张金山，姬国强，等. 基于ProCAST的拉伸试棒的金属型铸造工艺分析[J]. 特种铸造及有色合金，2010，30(9)：807-809.
Qiu B, Zhang J S, Ji G Q，et al. Analysis of permanent mold casting tensile testing bar based on ProCAST software[J]. Special Casting & Nonferrous Alloys, 2010，30(9):807-809.
[3]张晓光，韩文，韦洲，等. 基于ProCAST的支架铸件浇注系统优化设计[J]. 热加工工艺，2019，48(1)：95-97.
Zhang X G, Han W, Wei Z，et al. Optimal design of gating system of bracket castings based on ProCAST[J]. Hot Working Technology, 2019，48(1): 95-97.
[4]夏鹄翔，段文科，王琳，等. 基于华铸CAE铝合金铸造充型氧化夹杂数值模拟[J]. 特种铸造及有色合金，2018，38(9)：956-959.
Xia H X, Duan W K, Wang L，et al. Numerical simulation of the oxidation inclusion during filling process of the aluminum alloy casting based on the InteCAST software[J]. Special Casting & Nonferrous Alloys, 2018，38(9): 956-959.
[5]GB/T 1173—2013,铸造铝合金[S].
GB/T 1173—2013, Casting aluminum alloy[S].
[6]Liu Z Y, Mao W M, Wang W P, et al. Preparation of semi-solid A380 aluminum alloy slurry by serpentine channel[J]. Transactions of Nonferrous Metals Society of China, 2015, 25(5): 1419-1426.
[7]Chen Z Z, Mao W M, Wu Z C. Preparation of semi-solid aluminum alloy slurry poured through a water-cooled serpentine channel[J]. International Journal of Minerals, Metallurgy and Materials, 2012, 19(1): 954-960.
[8]Zhu W Z, Mao W M, Qin T U. Preparation of semi-solid 7075 aluminum alloy slurry by serpentine pouring channel[J]. Transactions of Nonferrous Metals Society of China, 2014, 24(4): 954-960.
[9]Zhao Z, Chen Q, Chao H, et al. Microstructural evolution and tensile mechanical properties of thixoforged ZK60-Y magnesium alloys produced by two different routes[J]. Materials & Design, 2009, 31(4): 1906-1916.
[10]Chen Z Z, Mao W M, Wu Z C. Mechanical properties and microstructures of Al alloy tensile samples produced by serpentine channel pouring rheo-diecasting process[J]. Transactions of Nonferrous Metals Society of China, 2011, 21(7): 1473-1479.
[11]Wang C J, Chen J Y, Shen Y Z. Melt mold casting process optimization of train coupler based on ProCAST[J]. Key Engineering Materials, 2018, 764: 312-322.
[12]Sun Z Z, Hu H, Chen X. Gating system design for a magnesium alloy casting[J]. Journal of Materials Science & Technology, 2008, 24(1): 93-95.
[13]李帅君，熊守美. 铝合金铸造充型过程气体和氧化膜卷入的数值模拟研究进展[J]. 铸造，2008，57(4)：321-326.
Li S J, Xiong S M. Research progress on modeling and simulation of air and oxide film entrapment during mold filling of aluminum casting[J]. Foundry, 2008，57(4): 321-326.
[14]Le V D, Morel F, Bellett D, et al. Multiaxial high cycle fatigue damage mechanisms associated with the different microstructural heterogeneities of cast aluminium alloys[J]. Materials Science and Engineering: A, 2016, 649: 426-440.
[15]沈月，何国球，田丹丹，等. 二次枝晶臂间距对A319铝合金拉伸及疲劳性能的影响[J]. 材料研究学报，2014，28(8)：587-593.
Shen Y, He G Q, Tian D D，et al. Effect of secondary dendrite arm spacing on tensile property and fatigue behavior of A319 aluminum alloy[J]. Chinese Journal of Materials Research, 2014，28(8): 587-593.
[16]Yang C L, Li Y B, Dang B, et al. Effects of cooling rate on solution heat treatment of as-cast A356 alloy[J]. Transactions of Nonferrous Metals Society of China, 2015, 25(10): 3189-3196.
[17]吴建华，周吉学，唐守秋，等. 冷却速率对铸态A356铝合金微观组织和拉伸性能的影响[J]. 功能材料，2016，47(A2)：63-66.
Wu J H, Zhou J X, Tang S Q，et al. Effects of cooling rate on microstructure and tensile properties of as-cast A356 alloy[J]. Journal of Functional Materials, 2016，47(A2): 63-66.
[18]程昌学，杨湘杰，何毅，等. Ce对A356合金的影响及细化机制的研究[J]. 稀有金属，2018，42(11)：1127-1133.
Cheng C X, Yang X J, He Y，et al. Properties of A356 aluminum alloy with Ce addition and its refining mechanism[J]. Chinese Journal of Rare Metals, 2018，42(11): 1127-1133.
[19]陈微，谷艳飞，董春法，等. 铝合金轮毂锻造组织缺陷有限元分析与工艺优化[J]. 锻压技术，2018，43(10)：36-42.
Chen W, Gu Y F, Dong C F，et al. Finite element analysis and process optimization on micro-defects of aluminum alloy wheel in forging[J]. Forging & Stamping Technology, 2018，43(10): 36-42.
|
|
服务与反馈：
|
|
【本网站尚未开通全文下载服务】【加入收藏】
|
|
|
|