5A06铝合金鞍型横梁等温挤压近净成形工艺

英文标题：Isothermal extrusion near-net forming process of saddle shaped beam for 5A06 aluminum alloy

作者：刘奇申红斌李保永高慧张素敏李信

分类号：TG376.2

出版年,卷(期):页码：2020,45(1):136-143

摘要：

针对某5A06铝合金鞍型横梁，设计了等温挤压近净成形试验。通过Deform有限元分析研究了鞍型横梁等温挤压过程中金属流动规律和缺陷产生原因，并进行了毛坯尺寸和热挤压件图的优化。设计了鞍型横梁等温挤压近净成形模具，可实现在普通压力机上加热管加热方式升温、成形后多顶杆同步脱模功能。通过等温挤压近净成形方法制备了长为580 mm、最薄壁厚为4 mm、筋高为8 mm、筋宽为6 mm的薄壁复杂多筋鞍型横梁，该构件90%以上部位尺寸精度可达到±0.3 mm，其余部位尺寸精度可达±0.5 mm，抗拉强度达340 MPa，伸长率约为25%。对等温挤压件装配部位进行少量机加，可获得3种不同尺寸的鞍型横梁。

For saddle shaped beam of 5A06 aluminum alloy, an isothermal extrusion near-net forming experiment was designed. Then, the metal flow law and the cause of defects in the isothermal extrusion process for saddle shaped beams were studied by finite element analysis Deform, and the blank size and the hot extrusion drawing were optimized. Furthermore, the isothermal extrusion near-net forming mold of saddle shaped beam was designed to realize the heating of heating pipe on the ordinary press and the simultaneous demoulding function of multi-rod after forming. Finally, a thin-walled complex multi-rib saddle shaped beam with the length of 580 mm, the thinnest wall thickness of 4 mm, the rib height of 8 mm and the rib width of 6 mm was obtained by the isothermal extrusion near-net forming method. And the dimensional accuracy for more than 90% of the saddle shaped beam reaches ±0.3 mm, while that of the other reaches ±0.5 mm. In addition, the tensile strength is 340 MPa, and the elongation is about 25%. Thus, the saddle shaped beams with three different sizes can be obtained by adding a small amount of machining to assembly parts of isothermal extrusion parts.

基金项目：

作者简介：刘奇（1990-），男，硕士，工程师 E-mail：liuqi3179@163.com

参考文献：

[1]付锦，戚文军，李亚江，等.Al-Mg-Si系铝合金汽车车身板的研究进展[J].材料研究与应用，2016，10(3): 159-166.

Fu J， Qi W J， Li Y J， et al.Research and development of Al-Mg-Si alloys in application of automotive body panel [J].Materials Research and Application, 2016, 10(3): 159-166.

[2]何建伟，王祝堂. 船舶舰艇用铝及铝合金 (1)[J].轻合金加工技术， 2015,43(9):1-11.

He J W， Wang Z T. Aluminum and its alloys for ships and naval vessels (1) [J]. Light Alloy Fabrication Technology，2015，43(9): 1-11.

[3]毕宝鹏,王勇,孙梦莹. 5A06铝合金超塑性变形力学特性[J]. 塑性工程学报,2015,22(2):62-67.

Bi B P, Wang Y, Sun M Y. Mechanical behavior of aluminum alloy 5A06 under superplastic deformation[J]. Journal of Plasticity Engineering,2015,22(2):62-67.

[4]文波,夏志单,季珊林,等. 复杂薄壁框类铝合金铸件工艺设计及数值模拟[J]. 特种铸造及有色合金,2018,38(7):768-771.

Wen B, Xia Z D, Ji S L,et al. Casting method design and numerical simulation of complex thin-wall aluminum alloy castings[J]. Special Casting & Nonferrous Alloys,2018,38(7):768-771.

[5]吉卫,周朝辉,曹海桥,等. 铝合金杯形件等温挤压成形工艺研究[J]. 热加工工艺,2007,36(5):69-72.

Ji W, Zhou Z H, Cao H Q, et al. Research of isothermal extrusion process for Al-alloy cup-shaped piece[J]. Hot Working Technology,2007,36(5):69-72.

[6]刘芳, 林忠钦, 单德彬, 等. 2A70 铝合金转子等温闭塞式锻造工艺研究[J]. 机械工程学报, 2005, 41(9): 161-165.

Liu F, Lin Z Q, Shan D B, et al. Research on the isothermal enclosed die forging of 2A70 aluminum rotor [J]. Chinese Journal of Mechanical Engineering, 2005, 41(9): 161-165.

[7]廖国防, 易幼平, 王少辉. 航空接头锻件等温锻压成形工艺[J]. 材料科学与工艺, 2012, 20 (1): 6-10.

Liao G F, Yi Y P, Wang S H. Isothermal forging forming process of aircraft adapter parts [J]. Material Science & Technology, 2012, 20(1): 6-10.

[8]胡传凯, 黄树海, 陈强, 等.轻合金等温精密成形工艺及应用[A].中国工程科技论坛第123场—2011国防科技工业科学发展论坛论文集[C].北京：北京核学会, 2011.

Hu C K, Huang S H, Chen Q, et al. Warm precision forming technology and application of light alloys[A].China Engineering Science and Technology Forum, No.123-Defense Industry Scientific Development Forum Proceedings in 2011 [C].Beijing:Chinese Muclear Society, 2011.

[9]张艳秋, 徐福昌, 单德彬, 等. 复杂盘饼类锻件等温精密成型工艺[J].航空制造技术, 2007, (S1): 460-465.

Zhang Y Q, Xu F C, Shan D B, et al. Isothermal precision forming technology of complex disk forgings[J]. Aeronautical Manufacturing Technology, 2007, (S1): 460-465.

[10]Xu J, Yang H, Li H, et al. Significance-based optimization of processing parameters for thin-walled aluminum alloy tube NC bending with small bending radius[J].Transactions of Nonferrous Metals Society of China, 2012,22(1):147-156.

[11]Zhang C S, Zhao G Q, Chen H, et al. Numerical simulation and metal flow analysis of hot extrusion process for a complex hollow aluminum profile[J]. International Journal of Advanced Manufacturing Technology, 2012, 60(1):101-110.

[12]Yang D Y, Park K, Kang Y S. Integrated finite element simulation for the hot extrusion of complicated Al alloy profiles[J].Journal of Material Process Technology,2001, 111(1-3):25-30.

[13]李峰, 林俊峰, 初冠南, 等. 铝合金锻件成形工艺及三维有限元分析[J]. 中国有色金属学报, 2009, 19(7): 1197-1202.

Li F, Lin J F, Chu G N, et al.3D finite element analysis and forging process of aluminum alloy forging parts[J]. The Chinese Journal of Nonferrous Metals, 2009, 19(7):1197-1202.

[14]GJB 1580A—2004，变形金属超声波检验方法[S].

GJB 1580A—2004，Ultrasonic inspection of wrought metal[S].

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】