组合形活塞销冷镦挤成形工艺
英文标题:Cold upsetting-extruding process for combination piston-pins
作者:隋毅 梁强 
单位:重庆科技学院 
关键词:活塞销 冷镦 冷挤压 等效应力 DEFORM-2D 
分类号:TG316
出版年,卷(期):页码:2020,45(1):109-113
摘要:

 针对组合形活塞销结构特征和工艺要求,分析该零件的成形难点为:两端圆锥孔的挤压成形和深径比大于2.5的中心圆孔反挤压。为此,应用DEFORM-2D有限元分析软件对组合形活塞销7工位冷镦挤成形工艺进行数值模拟分析。通过数值模拟分析和工艺方案修订,确定最终的成形工艺方案为:下料—整形—压凹—反挤压—冲孔—第1次挤锥—第2次挤锥,并采用硬质合金YG15制造反挤压凸模,以避免一次反挤压成形时凸模横截面变化处的折断。采用该方案进行工艺实验,实验结果表明:组合形活塞销尺寸满足零件设计要求,无折叠、开裂等锻造缺陷,深孔反挤压凸模使用寿命大于8万件。

 For structural characteristics and process requirements of combination piston-pins, its forming difficulties were analyzed as the extruding of tapered holes at both ends and the backward extrusion of central circular hole with a ratio of depth to diameter more than 2.5, and the cold upsetting-extruding process of combination piston-pins with seven steps was simulated and analyzed by finite element analysis software DEFORM-2D. Through the numerical simulation analysis and the revision of the process scheme, the final forming process scheme was determined as blanking-sizing-upsetting-backward extrusion-piercing-the first extruding taper holes-the second extruding taper holes, and the backward extrusion punch was made of YG15 cemented carbide to avoid breakage where the cross section of punch changed in the backward extrusion. Using the final process scheme for production experiment, the experiment result shows that the combination piston-pin meets the design requirements of part without forging defects such as fold and crack, and the backward extrusion punch of deep hole has a service life of more than 80000 pieces.

基金项目:
重庆市基础科学与前沿技术研究专项基金资助项目(cstc2017jcyjAX0175)
作者简介:
作者简介:隋毅(1981-),男,硕士,工程师 E-mail:suiyi_1981@qq.com
参考文献:

[1]胡慧玲, 林楚新. 某活塞销的断裂失效分析[J]. 热加工工艺, 2015,44(24): 226-228.


Hu H LLin C X. Analysis on fracture failure of piston pin [J]. Hot Working Technology2015,44(24)226-228.


[2]李炳, 陈伟, 李名尧,. 汽车活塞销温-冷复合挤压成形工艺研究[J]. 铸造技术, 2016,37(10): 2204-2207.


Li BChen W Li M Yet al. Study on warm and cold composite extrusion forming process for automobile piston pins [J]. Foundry Technology201637(10)2204-2207.


[3]梁强. 活塞销冷镦挤成形微折叠分析及改进措施[J]. 塑性工程学报, 2018, 25(6): 61-66.


Liang Q. Micro-folding defect analysis and improvement of cold upsetting-extruding process for piston-pin [J]. Journal of Plasticity Engineering, 2018, 25(6):61-66.


[4]Lee D J, Kim D J, Kim B M. New processes to prevent a flow defect in the combined forward-backward cold extrusion of a piston-pin [J]. Journal of Materials Processing Technology, 2003, 139(1)422-427.


[5]赵震, 陈军, 吴公明. 冷温热挤压技术[M]. 北京: 电子工业出版社, 2008.


Zhao Z, Chen J, Wu G M. Cold/Warm/Hot Extrusion Technology [M]. Beijing: Publishing House of Electronics Industry, 2008.


[6]詹艳然, 廖丹佩. 继电器Ag-Cu复合触点冷镦成形过程数值模拟分析[J]. 模具工业, 2015, 41(4): 11-15.


Zhan Y R, Liao D P. Numerical simulation analysis on cold heading process of relay with Ag-Cu composite contact [J]. Die & Mould Industry, 2015, 41(4): 11-15.


[7]隋毅, 梁强. 组合形活塞销冷镦挤成形工艺方案设计[J]. 锻压技术, 2019, 44(6)97-103.


Sui Y, Liang Q. Process design on cold upsetting and extruding for combination piston-pin [J]. Forging & Stamping Technology, 2019, 44(6):97-103.


[8]Lange K, Kammerer M, Pohlandt K, et al.挤压技术:金属精密件的经济制造技术[M].杜国辉, 赵震, . 北京: 机械工业出版社,2014.


Lange K, Kammerer M, Pohlandt K, et al.Extrusion Technology: Economical Manufacture Technology of Metal Precision Parts [M]. Translated by Du G HZhao Z. Beijing: China Machine Press, 2014.


[9]王德俊, 姚志英, 李艳红,. 活塞销冷挤压成形工艺研究[J]. 热加工工艺, 2011, 40(17)86-88.


Wang D JYao Z Y Li Y Het al. Study of cold extrusion forming process for piston pin [J]. Hot Working Technology2011, 40(17)86-88.


[10]张莉, 李升军. DEFORM在金属塑性成形中的应用[M]. 北京:机械工业出版社, 2009.


Zhang L, Li S J. DEFORM in the application of metal plastic forming[M]. BeijingChina Machine Press, 2009.


[11]胡建军. DEFORM-3D塑性成形CAE应用教程[M]. 北京:北京大学出版社, 2011.


Hu J J. DEFORM-3D Plastic Forming CAE Application Tutorial [M]. Beijing: Peking University Press, 2011.


[12]李金普, 丁存光, 李一, . 低压烧结温度对YG15粗晶硬质合金性能的影响[J]. 硬质合金, 2016, 33(1):33-37.


Li J P, Ding C G, Li Y, et al. Effect of sintering temperatures on performance of WC-15% Co coarse-grained cemented carbide by sinter-HIP[J]. Cemented Carbide, 2016, 33(1):33-37.


 

服务与反馈:
本网站尚未开通全文下载服务】【加入收藏
《锻压技术》编辑部版权所有

中国机械工业联合会主管 北京机电研究所有限公司 中国机械工程学会塑性工程分会主办
联系地址:北京市海淀区学清路18号 邮编:100083
电话:+86-010-82415085 传真:+86-010-62920652
E-mail: fst@263.net(稿件) dyjsjournal@163.com(广告)
京ICP备07007000号-9