2205双相不锈钢中厚板边部起皮缺陷机理研究

英文标题：Study on edge peeling defect mechanism of medium and heavy plate for 2205 duplex stainless steel

作者：任培东张有余纪显彬潘红涛

单位：酒钢集团

分类号：TG335

出版年,卷(期):页码：2019,44(9):33-39

摘要：

利用扫描电镜观察了2205双相不锈钢中厚板边部起皮缺陷,缺陷部位氧化皮的成分和形态有明显的差别，缺陷掉落后，凹坑内主要富集Cr、O、C元素。研究表明：2205双相不锈钢中厚板边部起皮缺陷与连铸坯边部柱状晶及受力状态有关。由于柱状晶强度低、面缩率低，中厚板展宽过程中位于连铸坯边部的柱状晶在拉应力作用下柱状晶晶界产生微裂纹，尤其是在α和γ两相结合部位易产生微裂纹，微裂纹在随后的轧制中扩展。同时，随着变形的深入，连铸坯在展宽轧制时的不均匀变形使连铸坯宽面上、下角部金属逐步向钢板心部流动，分别内移至钢板上、下表面，角部被氧化的金属进入钢板基体。经两种因素共同作用，在后续的轧制过程中微裂纹逐步扩展，导致缺陷的产生。

The edge peeling defect of medium and heavy plate for 2205 duplex stainless steel was analyzed by SEM, then it found that the composition and morphology of oxide scale in defect position had obvious differences,and the Cr,O,C elements were mainly enriched in the steel pit after defects dropped out.The results show that the edge peeling defect of medium and heavy plate for 2205 duplex stainless steel is relative to columnar crystal and force status at the edge of continuous casting billet.Because of the low strength and the reduction of area of columnar crystal, the crystal boundary of the columnar crystal which located at the edge of the continuous casting billet was engendered the microcrack under the effect of the tensile stress during the spreading procedure of the medium and heavy plate. In especial, the microcrack easily engendered at the combination position of the α and γ phase, then the crack extended in the subsequent rolling procedure. Meanwhile, with the penetration of the deformation, the metal at the upper and lower corner positions of the side section for billet flowed to the core of the steel plate gradually under the effect of the in-homogeneous deformation during the spreading rolling procedure of the continuous casting billet, then separately moved to the upper and lower surfaces of the billet, and the oxidized metal of the corner position entered into the matrix of the steel plate. The microcrack was extended gradually during the subsequent rolling procedure under the combined action of the two factors, and formed the defect.

基金项目：

任培东（1972-），男，硕士，正高级工程师 E-mail：renpeidong@jiugang.com 通讯作者：张有余（1970-），男，硕士，正高级工程师 E-mail：zhangyouyu@jiugang.com

参考文献：

［1］陈雷，王龙妹，杜晓建，等.2205双相不锈钢的高温变形行为
［J］.金属学报，2010，46（1）：52-56.

Chen L, Wang L M, Du X J, et al. Hot deformation behavior of 2205 duplex stainless steel
［J］. Acta Metallurgica Sinica, 2010, 46(1):52-56.

［2］方轶琉，程逸明，王月香，等.双相不锈钢热变形行为研究
［J］.东北大学学报：自然科学版，2009,30（8）：1124-1126.

Fang Y L, Cheng Y M, Wang Y X, et al. Hot deformation behavior of duplex stainless steels
［J］. Journal of Northeastern University: Natural Science, 2009, 30(8):1124-1126.

［3］张沛学，任学平，谢建新，等.双相不锈钢超塑性变形机理
［J］.北京科技大学学报，2005，27（1）：68-71.

Zhang P X, Ren X P, Xie J X, et al. Superplasticity mechanism of duplex stainless steels
［J］. Journal of University of Science and Technology Beijing, 2005, 27(1):68-71.

［4］宋红梅，丁秀平，刘雄，等.高温时效2205双相不锈钢中的组织转变
［J］.材料热处理学报，2010，31（3）：43-47.

Song H M, Ding X P, Liu X, et al. Microstructure evolution in a 2205 duplex stainless steel during aging at high temperature
［J］. Transaction of Materials and Heat Treatment, 2010, 31(3):43-47.

［5］王月香，程逸明，刘振宇，等.2205双相不锈钢中σ相的析出规律
［J］.钢铁研究学报，2009，21（10）：51-54.

Wang Y X, Cheng Y M, Liu Z Y, et al. Precipitation behavior of σ-phase in 2205 dual phase stainless steel
［J］. Journal of Iron and Steel Research, 2009, 21(10):51-54.

［6］韩英，邹德宁，李姣，等.双相不锈钢中σ相的析出及其数学模型
［J］.铸造技术，2009，30（6）：820-823.

Han Y,Zou D N,Li J,et al.Precipitation of sigma phase in duplex stainless steels and modeling
［J］.Foundry Technology,2009,30(6):820-823.

［7］毛萍莉,苏国跃,杨柯.0Cr17Mn14Mo2N双相不锈钢组织与性能的关系
［J］.材料热处理学报，2001，22(3)：19-22.

Mao P L,Su G Y,Yang K.The relationship of properties and microstructure of 0Cr17Mn14Mo2N duplex stain steel
［J］.Transactions of Materials and Heat Treatment,2001,22(3):19-22.

［8］舒先进，张淑琴，宋志刚.00Cr22Ni5Mo3N双相不锈钢热加工性能的试验研究
［J］.钢管，2004，33（6）：15-19.

Shu X J, Zhang S Q, Song Z G. Experimental research on hot workability of 00Cr22Ni5Mo3N dual phase stainless steel
［J］. Steel Pipe, 2004, 33(6):15-19.

［9］林刚，张志霞，宋洪伟.双相不锈钢高温微观变形行为
［J］.钢铁研究学报，2008，20（6）：41-44.

Lin G, Zhang Z X, Song H W. High temperature microscopic deformation behavior of duplex phase stainless steel
［J］. Journal of Iron and Steel Research, 2008, 20(6):41-44.

［10］王晓峰，陈伟庆，毕洪运，等.影响双相不锈钢热塑性的诸因素讨论
［J］.上海金属，2007，29（6）：37-41.

Wang X F,Chen W Q,Bi H Y,et al.Discussion on hot workability of duplex stainless steel
［J］.Shanghai Metals,2007,29(6):37-41.

［11］王建泽，钱张信，纪显彬.2205双相不锈钢表面起皮缺陷研究
［J］.热加工工艺，2016，45（17）：256-258.

Wang J Z,Qian Z X,Ji X B. Study on surface peeling defect of 2205 duplex stainless steel
［J］.Hot Working Technology,2016,45(17):256-258.

［12］李燕.2205双相不锈钢连铸板坯的高温力学性能研究
［D］.西安：西安建筑科技大学，2012.

Li Y. High Temperature Mechanical Properties of 2205 Duple Stainless Steel Billet
［D］.Xi′an：Xi′an University of Architecture and Technology，2012.

［13］张华，倪红卫.中厚板边裂的形成与控制
［J］.武汉科技大学学报：自然科学版，2006，29（3）：217-220.

Zhang H,Ni H W.Formation and control of edge cracks on medium and heavy plate
［J］. Journal of Wuhan University of Science and Technology：Natural Science Edition,2006,29(3):217-220.

［14］马忠伟，张慧，胡鹏，等.中厚板边部折叠模拟实验及机理研究
［J］.工程科学学报，2015，37（12）：1630-1636.

Ma Z W, Zhang H, Hu P, et al.Simulation experiments and mechanism of medium plate edge folding
［J］.Chinese Joural of Engineering,2015,37(12):1630-1636.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】