基于优化锥形锻造法的热锻润滑剂性能评价

英文标题：Evaluation of lubricating performance for hot forging lubricant based on optimized cone-forging method

作者：陈伦强郑俊涛庄晓伟胡成亮赵震

分类号：TG316

出版年,卷(期):页码：2018,43(1):154-159

摘要：

使用优化锥形锻造法对4种固体基体成分和含量不同的水基热成形润滑剂的润滑性能进行评价，得到了表征润滑剂润滑性能的H指标和F指标在950和1050 ℃条件下以及润滑剂原液和水按照体积比分别为1∶60，1∶20和1∶4.5这3种调配方案下的值。试验结果表明，优化锥形锻造法能够辨别不同润滑剂在不同条件下的性能差异。以复合硬脂酸盐为基体的润滑剂在不同条件下的润滑性能都较优，润滑性能稳定，工艺适用性好；而以人工石墨为基体的润滑剂的润滑性能普遍较差。原液中固体物含量较高的两种润滑剂在950 ℃锻造时,其润滑性能随着原液含量的增高而增大，两种非鳞片型石墨基润滑剂在1050 ℃ 锻造时的最佳配比为1∶20；润滑剂原液的粘度越大，润滑性能越好。

The lubricating performance of four kinds of solid matrixes contents and different contents of water-based thermoformed lubricants were evaluated by the optimized cone-forging method, and the values of H-indicator and F-indicator reflecting the lubricating performance of lubricant at 950 ℃ and 1050 ℃ with the volume ratios of lubricant and water of 1∶60, 1∶20 and 1∶4.5 were obtained. The results show that the optimized cone-forging method can indicate different lubricating performances of lubricants under varied conditions, and the lubricating performances of lubricants with compound stearate to be the matrix are the best under different conditions with stable lubricating performance and good process suitability. However, the lubricating performances of lubricants with artificial graphite to be the matrix are generally poor. Therefore, when two kinds of lubricants with high solid content in stock solution are forged at 950 ℃, their lubricating performances increase with the concentrations of stock solution. The optimal volume ratio of two kinds of lubricants with non-scale graphite to be the matrix forged at 1050 ℃ is 1∶20. The greater the viscosity of lubricant stock solution is, the better the lubricating performance is.

基金项目：

国家自然科学基金资助项目（51475294）

作者简介：陈伦强（1991-），男，硕士研究生，E-mail：chenlunqiang@sjtu.edu.cn；通讯作者：赵震（1972-），男，博士，教授，E-mail：zzhao@sjtu.edu.cn

参考文献：

[1]武东文，吴任东，袁朝龙，等.大口径钢管突破挤压力分析 [J].塑性工程学报, 2017, 24(1):24-29.

Wu D W，Wu R D，Yuan C L，et al.Analysis of breakthrough extrusion pressure for large scale steel pipe [J]. Journal of Plasticity Engineering, 2017, 24(1):24-29.

[2]吴顺达. 我国锻造行业模具与润滑现状及其发展方向 [J]. 模具工业, 2011, 37(5):5-11.

Wu S D. Status of die and lubrication of forging industry in China and its development trend [J]. Die & Mold Industry, 2011, 37(5):5-11.

[3]严晓华, 陈国需. 固体润滑技术的研究现状及展望 [J]. 能源研究与信息, 2005, 21(2):69-74.

Yan X H, Chen G X. Current development and future prospects on solid lubricating techniques [J]. Energy Research and Information, 2005, 21(2):69-74.

[4]卜军敏. 系列含磷水基润滑添加剂的合成及摩擦学性能研究[D]. 上海：上海交通大学, 2012.

Bu J M. The Synthesis and Tribological Characteristics of Series P-containing Additives in Water [D]. Shanghai: Shanghai Jiao Tong University, 2012.

[5]徐健, 庞学慧, 张治民. 水基润滑剂在温挤成形中的应用 [J]. 锻压技术, 2015, 40(1):104-107.

Xu J, Pang X H, Zhang Z M. Application of water-based lubricant in warm extrusion forming [J]. Forging & Stamping Technology, 2015, 40(1):104-107.

[6]李艳, 陈芳雷. 温热挤压用润滑剂实验研究 [J]. 热加工工艺, 2006, 35(17):12-13.

Li Y, Chen F L. Experiment study of special lubricant for warm-hot extrusion [J]. Hot Working Technology, 2006, 35(17):12-13.

[7]吕亚非, 马玉宁, 韩翎,等. 石墨在半金属摩擦材料中的作用及其对摩擦性能的影响 [J]. 北京化工大学学报：自然科学版, 2006, 33(5):58-61.

Lyu Y F, Ma Y N, Han L, et al. Role of graphite in semi-metallic friction materials and its effects on friction performance [J]. Journal of Beijing University of Chemical Technology：Natural Science Edition，2006, 33(5):58-61.

[8]杨帆, 董选普, 李伟华,等. 新型金属热模锻用非石墨型润滑剂的研究 [J]. 锻压技术, 2012, 37(2):125-128.

Yang F, Dong X P, Li W H,et al. Research on new kind of non-graphite based lubricant for metal hot forging [J]. Forging & Stamping Technology, 2012, 37(2):125-128.

[9]Hu C, Ou H, Zhao Z. An alternative evaluation method for friction condition in cold forging by ring with boss compression test [J]. Journal of Materials Processing Technology, 2015, 224:18-25.

[10]Li L X, Peng D S, Liu J A, et al. An experimental study of the lubrication behavior of A5 glass lubricant by means of the ring compression test [J]. Journal of Materials Processing Technology, 2000, 102(1):138-142.

[11]殷强，胡成亮，赵震. 基于多岛遗传算法的圆环镦粗测试方法优化 [J]. 锻压技术, 2017,42(5):108-112.

Yin Q, Hu C L, Zhao Z. Optimization on ring compression test based on multi-island genetic algorithm [J]. Forging & Stamping Technology, 2017, 42(5):108-112.

[12]Sofuoglu H, Rasty J. On the measurement of friction coefficient utilizing the ring compression test[J]. Tribology International, 1999, 32(6): 327-335.

[13]Buschhausen A, Weinmann K, Lee J Y, et al. Evaluation of lubrication and friction in cold forging using a double backward-extrusion process [J]. Journal of Materials Processing Technology, 1992, 33(1-2): 95-108.

[14]Zhang Q, Felder E, Bruschi S. Evaluation of friction condition in cold forging by using T-shape compression test [J]. Journal of Materials Processing Technology, 2009, 209(17): 5720-5729.

[15]Bennett C J. A comparison of material models for the numerical simulation of spike-forging of a CrMoV alloy steel [J]. Computational Materials Science, 2013, 70:114-22.

[16]Hu C L, Ou H G, Zhao Z. Investigation of tribological condition in cold forging using an optimized design of spike forging test [J]. Advances in Mechanical Engineering, 2015, 7(5): 1-11.

[17]胡成亮, 赵震. 锥形锻造润滑效果检测装置及方法 [P]. 中国：CN103776989A, 2014-05-07.

Hu C L, Zhao Z. Device and method for detecting conical forging lubricating effect [P]. China: CN103776989A, 2014-05-07.

[18]Yang L, Shivpuri R. Spreading behavior of water based graphite lubricants on hot die surfaces [J]. CIRP Annals-Manufacturing Technology, 2006, 55(1): 299-302.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】