锻压技术

70Cr3Mo钢支承辊超探不合格原因分析及改进措施

英文标题：Analysis on disqualification reason and improvement measures of steel 70Cr3Mo back-up roll by ultrasonic inspection

作者：陆宝山王雷刚季业益

单位：苏州工业职业技术学院江苏大学

关键词：支承辊大锻件超声波探伤着色渗透检验金相试验非金属夹杂物

分类号：TG316.1

出版年,卷(期):页码：2017,42(7):6-13

摘要：

制造44800和19500 kg的两根70Cr3Mo钢支承辊大锻件。钢锭采用EAF+LF+VD+VC冶炼浇注，1锭锻制2件，锻后球化退火，出炉冷却后，毛坯进行超声波探伤检查。结果发现：小辊超探合格踩线，大辊在冒口端辊颈部分存在超标缺陷。为了探究锻造工艺合理性，切掉大辊两端辊颈部分，利用辊身合格的坯料改锻成小辊。改锻后的小辊经超声波探伤发现，除辊身外两端辊颈部分均存在超标密集缺陷。通过一系列试验，对孔洞缺陷和夹杂物进行了分析，确定了导致支承辊超探不合格的原因：铸锭缺陷中广泛分布的非金属夹杂物分割了钢基体的连续性，恶化了钢的性能，导致超探不合格。此外，分析了夹杂物的来源及其危害性，并提出了相应的工艺改进措施。

Two back-up roll forgings of steel 70Cr3Mo with the weight of 44800 kg and 19500 kg were respectively made. The ingot was melted and poured by the EAF+LF+VD+VC method, and one ingot was forged into two pieces. After spheroidizing annealing and cooling, the blanks were checked through ultrasonic inspection. The result shows that the light roll is up to standard, but there are excessive defects in the roll neck of the heavy one. In order to explore the technological rationality of forging, two ends of the heavy roll neck part were cut to forge a new light back-up roll based on the qualified body. Nevertheless, there are still overproof defects in the roll neck of the new one except the roll barrel. Thus, the hole defects and inclusions were analyzed by a series of experiments, and the reasons for the disqualification of the back-up roll were determined after ultrasonic inspection. Furthermore, the non-metallic inclusions in the ingot widely distributing on the defect split the continuity of the steel matrix and deteriorate the steel performance, which result in the disqualification of ultrasonic inspection. In addition, the source and harmfulness of non-metallic inclusions were analyzed and the corresponding improvement measures were put forward to prevent such defects.

基金项目：

国家自然科学基金资助项目（51275216）；2017年度苏州工业职业技术学院院级课题资助项目（SGYKJ201708）；江苏高校品牌专业建设工程资助项目（PPZY2015B186）

作者简介：陆宝山(1981-)，男，博士研究生，E-mail：lubs@siit.edu.cn；通讯作者：王雷刚(1963-)，男，教授，博士生导师，E-mail：lgwang@mail.ujs.edu.cn

参考文献：

[1]康大韬，叶国斌. 大型锻件材料及热处理 [M]. 北京: 龙门书局, 1998.

Kang D T, Ye G B. Large Forging Material and Heat Treatment [M]. Beijing: Longmen Publishing House, 1998.

[2]刘助柏. 大锻件形变新理论与新工艺 [M]. 北京：机械工业出版社, 2009.

Liu Z B. New Deformation Theory and Technology of Large Forgings [M]. Beijing: China Machine Press, 2009.

[3] JB/T 4120—2006, 大型锻造合金钢支承辊技术标准[S].

JB/T 4120—2006, Heavy forged alloy steel back up rolls[S].

[4]吕炎. 锻件缺陷分析与对策 [M]. 北京: 机械工业出版社, 1999.

Lyu Y. Analysis and Countermeasures of Forging Defects [M]. Beijing: China Machine Press, 1999.

[5]Nisha S Cyril, Ali Fatemi. Experimental evaluation and modeling of sulfur content and anisotropy of sulfide inclusions on fatigue behavior of steels [J]. International Journal of Fatigue, 2009, 31(11): 526-537.

[6]Taizo Makino. The effect of inclusion geometry according to forging ratio and metal flow direction on very high-cycle fatigue properties of steel bars [J]. International Journal of Fatigue, 2008, 30(6): 1409-1418.

[7]Kiessling R. Nonmetallic inclusions and their effects on the properties of ferrous alloys [J]. Encyclopedia of Material Science and Technology, 2001,7(5): 6278-6283.

[8]朱怀沈，聂义宏，白亚冠，等. 700 ℃先进超超临界汽轮机转子用617合金锻造工艺研究 [J]. 锻压技术，2016, 41(9): 7-12.

Zhu H S, Nie Y H, Bai Y G, et al. Investigation on the hot forging process of alloy 617 A-USC steam turbine rotors at 700 ℃ [J]. Forging & Stamping Technology, 2016, 41(9): 7-12.

[9]乙继海，王杰，刘贺，等. 45Cr4NiMoV支承辊轴颈根部裂纹原因分析 [J]. 一重技术, 2011, (2): 27-30.

Yi J H, Wang J，Liu H, et al. Crack cause analysis happened on root of 45Cr4NiMoV back-up roll neck [J]. CFHI Technology, 2011, (2): 27-30.

[10]史宇麟. 大锻件两次镦拔锻造的工艺优化[J]. 热加工工艺, 2007,36(5):51-53.

Shi Y L. Optimizing on forging process of two-time upsetting and stretching [J]. Hot Working Technology, 2007, 36(5): 51-53.

[11]王以华，吴振清，陈修琳，等. 型砧几何尺寸对大锻件锻造孔隙闭合的影响[J]. 金属加工, 2013, (1): 22-25.

Wang Y H, Wu Z Q, Chen X L, et al. Effects of swage geometry size on the pore closure of large forgings [J]. Metal Working, 2013, (1): 22-25.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】