基于载荷下降法的双相钢DP590拉深减薄率研究

英文标题：Research on the thinning rate of dual phase steel DP590 in deep drawing based on the load drop method

作者：沙洵杨伟龙吴浩陈炜

单位：江苏大学

分类号：TG113.25

出版年,卷(期):页码：2017,42(3):144-148

摘要：

采用载荷下降法研究了双相钢DP590在不同压边力下拉深成形的减薄率。采用BCS-50AR通用板材成形性试验机进行有无润滑条件的对比拉深试验，获得成形力-凸模位移关系曲线。试验结果发现，拉深件凸缘部位和凹模圆角处的润滑有利于拉深成形，而无润滑条件下的拉深容易破裂。拉深件凸缘部位增厚，凹模圆角处和筒壁部位均有不同程度的减薄。危险断面处的减薄率最大，破裂情况下的最小减薄率为28.6%，无破裂情况下的最大减薄率为19.3%，达到实际生产要求。

The thinning rates of dual phase steel DP590 under different blank holder forces in deep drawing were studied by the load drop method. Then, the comparative deep drawing tests with and without lubrication condition were carried out by the BCS-50AR universal sheet metal forming machine, and the relationship curve between the forming force and the punch displacement was obtained. The results show that the lubrication at flange and die fillet of the drawing part is conducive to drawing forming, and the drawing is broken easily without lubrication. Thus, the thickness of flange of the drawing part increases, and the thickness of die fillet and the cylinder wall are reduced by a certain degree. Furthermore, on the dangerous section, the minimum thinning rate is 28.6% with rupture, and the maximum thinning rate is 19.3% without rupture, which can meet the production requirements.

基金项目：

沙洵(1990-)，男，硕士研究生陈炜(1965-)，男，博士，教授

参考文献：

［1］马鸣图，Shi M F. 先进的高强度钢及其在汽车工业中的应用[J]. 钢铁，2004，39（7）：68-72.Ma M T, Shi M F. Advanced high strength steel and its application in automobile industry[J]. Iron and Steel, 2004, 39(7):68-72.
［2］康永林，陈贵江，朱国明，等. 新一代汽车用先进高强钢的成形与应用[J]. 钢铁，2010，45（8）：1-6.Kang Y L, Chen G J, Zhu G M, et al. Forming technology and application of new generation advanced high strength steel for automobile[J]. Iron and Steel, 2010, 45(8):1-6.
［3］程令霞，曹阳根，邓沛然，等.冲压速度对DP780双相钢和304不锈钢胀形性能影响的试验对比分析[J]. 锻压技术，2015，40（2）：145-147.Cheng L X，Cao Y G，Deng P R，et al. Experimental comparative analysis for influence of punch speed on bulging performance of DP780 dual phase steel and 304 stainless steel [J]. Forging & Stamping Technology，2015，40（2）：145-147.
［4］邓俊彦，冷星环，吴恺威，等.冲压速度对双相钢B340/590DP拉深成形性能的影响[J]. 锻压技术，2016，41（7）：109-113.Deng J Y，Leng X H，Wu K W, et al. Effect of stamping speed on drawing performance of dualphase steel B340/590DP[J]. Forging & Stamping Technology，2016，41（7）：109-113.
［5］蒋浩民，陈新平，石磊，等. 先进高强度钢板的冲压成形特性及其应用[J]. 塑性工程学报，2009，16（4）：183-186.Jiang H M，Chen X P，Shi L, et al.Forming characteristics and application of advanced high strength steel[J]. Journal of Plasticity Engineering, 2009, 16(4):183-186.
［6］蒋浩民, 陈庆欣, 苏海波,等.双相钢板成形性能试验研究[J]. 锻压技术，2007，32（6）：76-78.Jiang H M, Chen Q X, Su H B, et al.Experimental study on the formability of dual phase steel[J].Forging & Stamping Technology, 2007, 32(6): 76-78.
［7］牛建辉, 朱平, 郭永进. 热镀锌双相钢 DP590 力学特性及其本构模型[J]. 上海交通大学学报, 2010, 44（10）：1382-1387.Niu J H，Zhu P，Guo Y J. Mechanical properties of hotdip galvanized dual phase steel DP590 and its constitutive model[J]. Journal of Shanghai Jiaotong University, 2010, 44(10): 1382-1387.
［8］舒建, 刁可山, 吴向东, 等. 温热环境下汽车用钢DP590板材屈服行为[J]. 塑性工程学报, 2015, 22（1）： 66-71.Shu J, Diao K S, Wu X D, et al.Study on yield behavior of automobile steel DP590 under thermal environment[J]. Journal of Plasticity Engineering, 2015, 22(1): 66-71.
［9］张召桃,平申. 杯突试验终点判别的载荷下降法[J]. 锻压技术，1988，13（1）：16-19.

Zhang Z T, Ping S. Drop in load as criterion of rupture in cupping test[J]. Forging ＆ Stamping Technology, 1988,13(1): 16-19.
［10］宝钢集团.冷轧产品手册[M].上海：宝钢集团，2008.Baosteel Group. Manual of ColdRolled Products[M]. Shanghai: Baosteel Group, 2008.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】