镁合金热连轧过程数值模拟

英文标题：Numerical simulation of hot tandem rolling process for magnesium alloy

作者：支晨琛张秀芝薛康

单位：太原科技大学

分类号：TG146.22

出版年,卷(期):页码：2016,41(2):144-147

摘要：

针对镁合金热连轧过程中已发生边裂的问题，采用ANSYS变形热力耦合数值分析法，对AZ31镁合金板在350 ℃、0.5 m·s-1 轧制速度下的三道次连轧过程进行了有限元模拟，并应用LS-DYNA后处理器对轧制过程中镁板不同部位的温度、应力分别进行了分析，并对模拟结果进行实验验证。研究结果表明：热连轧过程中，首道次镁板温降值较大，而且不同位置的温降幅值不同；此外，轧制过程中镁板边部中心层应力始终大于中部表层应力值。轧制过程中温度的不均匀变化以及边部应力集中使得镁合金在热连轧过程中易于发生边裂。

For the problem of edge crack in hot tandem rolling of magnesium alloy, the process of three passes tandem rolling for magnesium alloy AZ31 sheet was simulated by ANSYS with the thermo-mechanical coupled analysis at temperature 350 ℃ and rolling speed 0.5 m·s-1. Furthermore, the temperature and stress in different parts of the magnesium plate were analyzed by LS-DYNA in the rolling process, and the simulation result was verified by the experiment. The research results show that in the hot tandem rolling, the temperature drop of magnesium plate is greater on the first pass, and they are varied on different parts. Moreover, the stress of center layer edge is greater than that of the middle surface layer in the rolling process. Due to change of non-uniform temperature and the edge stress concentration, the edge crack of magnesium alloy plate occurs easily in the hot tandem rolling.

基金项目：

国家自然科学基金资助项目(51105264)；太原科技大学研究生科技创新项目（20145005）

支晨琛（1989-），女，硕士研究生张秀芝（1973-），女，博士，副教授

参考文献：

[1]陈振华.变形镁合金[M].北京：化学工业出版社，2004.Chen Z H. Wrought Magnesium Alloy[M]. Beijing：Chemical Industry Press, 2004.

[2]丁文江.镁合金科学与技术[M].北京：科学出版社，2007.Ding W J. Science and Technology of Magnesium Alloys[M]. Beijing：Science Press, 2007.

[3]阚盈, 刘振刚, 张士宏,等. 基于真实微观结构的SiCp/Al复合材料轧制过程模拟[J]. 稀有金属, 2015,39(4):289-299.Kan Y, Liu Z G, Zhang S H, et al.Rolling process simulation of SiCp/Al composites via a microstructure-based model [J].Chinese Journal of Rare Metals, 2015,39(4):289-299.

[4]李建平, 车路长. AZ80镁合金深孔筒形件数值模拟及试验研究[J]. 锻压技术, 2014, 39(5):66-72.Li J P, Che L C. Numerical and experimental investigation of deep hole cylindrical component of AZ80 magnesium alloy
［J］．Forging ＆ Stamping Technology，2014,39(5):66-72.

[5]Zhang D F, Dai Q W, Fang L，et al. Prediction of edge cracks and plastic damage analysis of Mg alloy sheet in rolling [J]. Transaction of Nonferrous Metals society of China, 2011, 21(5):1112-1117.

[6]陈昊, 袁任枢，宋德锋.温度及挤压速度对镁合金应力影响的模拟[J].特种铸造及有色合金，2014,34（4）：367-370.Chen H, Yuan R S, Song D F. Simulation on influence of temperature and speed of static liquid extrusion on stress in magnesium alloy[J]. Special Casting & Nonferrous Alloys, 2014, 34（4）：367-370.

[7]李毓英. AZ31镁合金小直径薄壁管拉拔工艺及性能研究[J]. 锻压技术, 2015, 40(5):59-62.Li Y Y. Research on drawing process and properties of AZ31 magnesium alloy tube with minor diameter and thin wall
［J］．Forging ＆ Stamping Technology，2015, 40(5) :59-62.

[8]张建新，高爱华，郭学锋，等. Mg-xSn-2Al-1.5Zn-0.8Si(x=3,5,8)合金的组织和性能[J]. 稀有金属, 2014，38(6): 967-972.Zhang J X, Gao A H, Guo X F, et al. Microstructure and properties of Mg-xSn-2Al-1.5Zn-0.8Si(x=3,5,8) magnesium alloys [J]. Chinese Journal of Rare Metals,2014，38(6):967-972.

[9]岳重祥，吴圣杰，曹垒，等. 冷轧薄板边损边裂原因概述及实例分析[J].锻压技术，2014,39(11):107-111.Yue C X,Wu S J, Cao L, et al. Cause summary and case analysis of edge crack defects during the cold rolling process of thin steel sheet[J]. Forging ＆ Stamping Technology, 2014,39（11）：107-111.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】