一种考虑剪切作用机制的Johnson-Cook断裂准则

英文标题：A modified Johnson-Cook fracture criterion considering shear effect

作者：诸楠赵震庄新村

单位：上海交通大学

分类号：TG311

出版年,卷(期):页码：2015,40(8):127-131

摘要：

基于已有的Johnson-Cook断裂准则，提出了新的考虑剪切作用机制的断裂准则。设计了不同温度、不同应变速率以及不同应力三轴度下的试验，对不同试验条件下的宏观断口进行分析。试验结果表明，随着温度的升高和应变速率的增大，断裂时刻的断裂应变减小。结合有限元模拟，确定了新的断裂准则中的断裂参数，获得了新的断裂准则。利用ABAQUS子程序功能将新的断裂准则嵌入有限元软件，并对高速棒料剪切工艺进行有限元模拟，模拟结果可以较好地表征棒料剪切断口的宏观特征，对比有限元模拟与试验的载荷-位移曲线验证了新的断裂准则的可靠性。

A new fracture criterion considering shear effect was proposed based on Johnson-Cook fracture criterion. Experiments under different temperatures, strain rates and stress triaxiality were designed and carried out. Macro fractures under different conditions were analyzed. Results show that fracture strain at the fracture time decreases with the increase of temperature and strain rate. New fracture criterion was obtained and parameters were determined by FEM software. It was embedded in FEM software by ABAQUS subroutine. The cutting process of high speed bar was simulated numerically. FEM results show good consistency with experimental features and the new fracture criterion is validated by comparison of load-displacement curves obtained from FEM and experimental results.

基金项目：

国家科技重大专项（2013ZX04002081）

诸楠（1990-），男，硕士研究生赵震（1972-），男，博士，教授，博士生导师

参考文献：

［1］虞松, 冯维明, 王戎. 金属韧性断裂准则的实验研究[J]. 锻压技术, 2010, 35(1): 121-124.Yu S, Feng W M, Wang R. Research on ductile fracture criterion in plastic deformation processes [J]. Forging & Stamping Technology, 2010，35 (1): 121-124.
［2］赵震, 庄新村, 向华, 等. 精密冲裁成形仿真技术研究进展[J]. 锻压技术, 2008, 33(1): 6-8.Zhao Z, Zhuang X C, Xiang H, et al. Advances in forming simulation for fine-blanking process [J]. Forging & Stamping Technology, 2008, 33(1): 6-8.
［3］陈志英, 董湘怀. GTN 细观损伤模型参数对板料损伤行为的影响[J]. 锻压技术, 2012,37(3): 23-27.Chen Z Y, Dong X H. Influence of GTN meso-damage model parameters on sheet forming damage behavior [J]. Forging & Stamping Technology, 2012,37(3): 23-27.
［4］王光艳, 梅益, 陈浪, 等. 42CrMo 环件轧制成形的数值模拟与分析[J]. 锻压技术, 2014,39(5):82-86.Wang G Y, Mei Y, Chen L. Numerical simulation and analysis of rolling forming of 42CrMo rings [J]. Forging & Stamping Technology, 2014,39(5):82-86.
［5］Brünig M, Chyra O, Albrecht D, et al. A ductile damage criterion at various stress triaxialities [J]. International Journal of Plasticity, 2008, 24(10): 1731-1755.
［6］黄建科, 董湘怀. 金属韧性断裂准则的数值模拟和试验研究[J]. 材料科学与工艺, 2010,18 (4): 450-454.Huang J K, Dong X H. Numerical simulation and experimental verification of ductile fracture criteria of metals[J]. Materials Science & Technology, 2010,18(4):450-454.
［7］Huespe A E, Needleman A, Oliver J, et al. A finite thickness band method for ductile fracture analysis[J]. International Journal of Plasticity, 2009, 25(12): 2349-2365.
［8］于忠奇, 杨玉英, 王永志, 等. 基于韧性断裂准则的铝合金板材成形极限预测[J]. 中国有色金属学报, 2003, 13(5) :1224-1226.Yu Z Q, Yang Y Y, Wang Y Z, et al. The prediction of forming limit of aluminum sheet based on ductile fracture criterion [J]. The Chinese Journal of Nonferrous Metals, 2003, 13(5):1224-1226.
［9］陈劼实, 周贤宾. 板料成形极限预测新判据[J]. 机械工程学报, 2009, 45(4): 64-69.Chen J S, Zhou X B. New forming limit criterion for sheet metals[J]. Journal of Mechanical Engineering, 2009, 45(4)：64-69.
［10］Johnson G R, Cook W H. Fracture characteristics of three metals subjected to various strains, strain rates, temperatures and pressures[J]. Engineering Fracture Mechanics, 1985, 21(1): 31-48.
［11］Lou Y, Huh H, Lim S, et al. New ductile fracture criterion for prediction of fracture forming limit diagrams of sheet metals[J]. International Journal of Solids and Structures, 2012, 49(25): 3605-3615.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】