Docol 1200M超高强钢板温成形性能研究

英文标题：Research on warm forming property of Docol 1200M ultra high strength steel

作者：龙军峰赵阳吕琳邓明

单位：重庆理工大学

分类号：TG316

出版年,卷(期):页码：2014,39(2):37-40

摘要：

高强钢板的温成形可显著改善高强钢的成形性能。以Docol 1200M超高强度钢板为对象，研究了高强钢在不同温度下的温成形性能，并对其相应的断口面进行了分析。结果表明：Docol 1200M超高强度钢板的拉胀成形性能总体随温度的升高而升高，但在200和300 ℃时，材料受到第一类回火脆性和蓝脆的影响，其成形性能突然降低；且此种高强钢板最适合的温成形温度为400 ℃。

Warm forming technology can significantly improve the formability of high strength steel. Docol 1200M ultra high strength steel was targeted, the warm forming property of Docol 1200M ultra high strength steel was studied at different temperatures, and the corresponding fracture surface was analyzed. The result shows that the warm drawing and bulging forming property of Docol 1200M ultra high strength steel rises overall with temperature increasing. However, its formability suddenly drops for the first kind of temper brittleness and blue brittleness at 200 and 300 ℃.The most suitable forming temperature of high-strength steel plate is 400 ℃.

基金项目：

重庆市教委科学技术研究项目（KJ110824）

龙军峰(1979-)，男，学士，讲师

参考文献：

［1］朱文英.汽车轻量化与高强度钢板的开发进展[J].上海金属，2003，25(4):11-15.Zhu Wenying. Development progress on ultralight steel and high strength steel sheet for automobile[J]. Shanghai Matels，2003,25(4):11-15.
［2］GB/T 15825.8-1995.金属薄板成形性能与试验方法成形极限图(FLD)试验[S]. GB/T 15825.8-1995.Sheet metal formability and test methodsForming limit diagram(FLD)test[S].
［3］崔忠.金属学与热处理[M].北京：机械工业出版社,2007.Cui Zhong.Metallography & Heat Treatment[M]. Beijing:China Machine Press ,2007.
［4］严玲. 汽车用TWIP钢的力学性能与微观组织[J].北京科技大学学报，2006,28（8）:739-743.Yan Ling. Properties and microstructure of TWIP steel used in automobiles[J].Journal of University of Science and Technology Beijing, 2006,28（8）:739-743.
［5］郑华. 1000 MPa级低碳马氏体钢的微观组织与力学性能[J].钢铁研究，2008,36（6）:52-54.Zheng Hua. The microstructure and mechanical properties of low carbon martensite steel with tensile strength of about 1000 MPa[J]. Research on Iron & Steel,2008,36（6）:52-54.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】