锻压技术

初始应变速率对00Cr22Ni5Mo3N双相不锈钢

英文标题：Effect of initial strain rate on superplasticity of 00Cr22Ni5Mo3N duplex stainless steel

作者：李少峰任学平李殊霞夏廷辉

分类号：TG331

出版年,卷(期):页码：2013,38(5):158-161

摘要：

对00Cr22Ni5Mo3N双相不锈钢经过固溶处理和冷轧变形后，在950 ℃下保温5 min，以不同的初始应变速率进行恒温超塑性拉伸试验，研究初始应变速率对00Cr22Ni5Mo3N双相不锈钢超塑性的影响规律。计算m值并观察不同初始应变速率下拉断后的组织，研究m值和断后组织随初始应变速率的变化规律，揭示初始应变速率影响材料超塑性的原因。试验结果表明：初始应变速率较低时，材料的组织比较粗大，初始应变速率增大时，材料的组织变得细小均匀。随着初始应变速率的增大，材料的伸长率和m值呈现相同的变化趋势，都是先增大后减小，并在1.5×10-3 s-1时所取得最大值分别为1070%和0.65。

After solution treatment and cold rolling deformation of 00Cr22Ni5Mo3N, super plastic deformation was tested with different initial strain rates for 5 min insulation under 950 ℃. Effect of initial strain rate on the super-plasticity of 00Cr22Ni5Mo3N duplex stainless steel was researched. The m-value was calculated and the microstructure after the tensile test was observed,and the variation of m-value and microstructure along with the initial strain rate was studied. The results show that when the initial strain rate is low, the microstructure becomes coarsely, on the contrary, the microstructure becomes fine. When the initial strain rate increases, variations of elongation and the m-value show the same tendency which increase first and then decrease. When the initial strain rate is 1.5×10-3 s-1, the elongation and the m-value achieve the maximum value of 1070% and 0.65 respectively.

基金项目：

李少峰（1966-），男，博士研究生

参考文献：

［1］孙文山.双相不锈钢的进展及其在工业中的应用[J].兵器材料科学与工程，2001，24(4)：50-53.Sun W S. Progress in duplex stainless steel and its application in industry [J]. Ordnance Material Science and Engineering, 2001, 24(4):50-53.
［2］Tersmeden K. Successful use of stainless steels in nitrogen-based fertilizer plants [J]. Process Safety Progress, 1997, 16(2): 110-116.
［3］Jimenez J A, frommeyer G, Carsi M, et al. Superplastic properties of a δ/γ stainless[J] . Materials Science and Engineering A, 2001, 307: 134-142.
［4］Miyamoto H, Mimaki T, Hashimoto S. Superplastic deformation of micro-specimens of duplex stainless steel [J]. Materials Science and Engineering A, 2001, 319-321: 779-783.
［5］何天荣.双相不锈钢及其特殊性能与应用[J].南方金属，2005，(1):1-3. He T R. Properties and applications of dual-phase stainless steels [J]. Southern Metals, 2005, (1):1-3.
［6］叶国平.双相不锈钢在含氯介质中的应用探讨[J].硫磷设计与粉体工程，2007，(1):35-37. Ye G P. Discussion of application of biphase stainless steel in cl-containing medium [J]. Sulphur Phosphorus & Bulk Materials Handling Related Engineering, 2007, (1):35-37.
［7］李春树.双相不锈钢及其在炼油工业中的应用[J].金属腐蚀控制，2003，17(5):12-14. Li C S. Duplex stainless steel and its application in oil refinery [J]. Total Corrosion Control, 2003, 17(5):12-14.
［8］Pinol-Jufz A, Iza-Mendia A, Gutierrez I. δ/γInterface boundary sliding as a mechanism for strain accommodation during hot deformation in a duplex stainless steel[J]. Metallurgical and MaterialsTransactions, 2000, 31A (6):16-17.
［9］Matsushita M, Ogiyama H, Suko T, et al. Study on solid-phase welding of duplex stainless steel with carbon steel based on superplasticity and consideration of the cyclic fatigue fracture behavior[J]. Materials Chemistry and Physics, 2009, 114(2-3): 599-603.
［10］张沛学，任学平，谢建新，等.双相不锈钢超塑性变形机理[J].北京科技大学学报，2005,27 (1):68-71. Zhang P X, Ren X P, Xie J X, et al. Superplasticity mechanism of duplex stainless steels [J].Journal of University of Science and Technology Beijing, 2005, 27 (1):68-71.
［11］Sinha V, Srinivasan R, Tamirisakandala S, et al. Superplastic behavior of Ti-6Al-4V-0.1B alloy [J]. Materials Science and Engineering A, 2012, 539(3): 7-12.
［12］Zelin M G. Processes of microstructural evolution during superplastic deformation [J]. Materials Characterization, 1996, 379(5): 311-329.
［13］Portnoy V K, Novikov I I. Evaluation of grain boundary sliding contribution to the total strain during superplastic deformation[J]. Scripta Materialia, `1998, 40(1): 39-43.
［14］Haslam A J, Yamakov V, Moldovan D, et al. Effects of grain growth on grain-boundary diffusion creep by molecular-dynamics simulation [J]. Acta Materialia, 2004, 52(7): 1971-1987.
［15］Wadsworth J, Ruano A O, Sherby D O. Denuded zones, diffusional creep, and grain boundary sliding [J]. Metallurgical and Materials Transactons, 2002, 33(2): 219-229.
［16］宋玉泉，程永春，刘术梅. 超塑性拉伸变形应变速率敏感性指数的试验测量及其精细分析[J]. 机械工程学报，2001，37(4):1-7.Song Y Q, Cheng Y C, Liu S M. experimental measurement and elaborate analysis of strain-rate sensitivity exponent in tensile forming [J]. Chinese Journal of Mechanical Engineering, 2001, 37(4):1-7.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】