锻压技术

TC4盘件双面辗压的实验研究

英文标题：Experimental study on double-sided roll forming of TC4 disk

作者：张风光金泉林李洪波

分类号：TG335

出版年,卷(期):页码：2013,38(5):87-91

摘要：

对TC4盘件进行高温双面辗压成形实验研究，观察了辗压后盘件的形状变化和微观组织分布。实验确认TC4盘件热辗压与铅盘室温辗压具有类似的形状变化特征，呈现出盘件直径增大、辗压槽两侧厚度增加、辗压槽出现“甩高”现象等。辗压后盘件微观组织分析结果表明，温度和变形对盘件微观组织变化有显著影响，因此盘件不同部位微观组织有明显差别：盘外缘温度偏高，变形量较小，组织处于相区；盘中心温度偏低，变形量较小，组织处于α+β相区；辗压槽及附近区域温度基本均匀为930 ℃，组织上处于β区，该区内材料变形差别较大，槽表面变形比槽中心大得多，组织上表现为初生α组织减少，并且槽表面比槽中心有更多的初生α组织转变为β相。

An experimental study on hot double-sided roll forming of TC4 titanium alloy disk was presented. The shape change and microstructure distribution of the deformed disk were observed in the forming experiment. It is found out that the shape change character of the TC4 disk hot rolled is similar to that of the lead disk coldly rolled. The main shape changes include a disk diameter increase, a local thickness increase near groove positions, and the “shuaigao” phenomena. It is also found out that the temperature and the deformation have significant effect on the microstucture of disk, so there is obvious difference in microstructure evolution in different positions of the disk. For example, in the disk fringe, the microstructure state is in β phase region due to high temperature and small strain; in the region near the disk center, the microstructure state is in α+β phase region due to lower temperature and small strain; in the transition region, the microstructure state is in α+β phase region due to middle temperature (930 ℃) and large strain, the deformation in groove surface is much bigger than that in groove center, the α phase decreases and there is more α phase in groove surface translated into β phase than that in groove center.

基金项目：

国家973计划资助项目（2011CB606306-3）;国家自然科学基金资助项目(50975116)

张风光（1987-），男，硕士研究生

参考文献：

［1］金泉林，刘晓飞，张艳姝.盘形件辗压成形原理及其数值模拟[J].钢铁研究学报，2003，15(Z1)：654-658.Jin Q L, Liu X F, Zhang Y S.Mechanism of roll forming of discal parts[J]. Journal of Iron & Steel Research, 2003,15(Z1):654-658.
［2］李彤，金泉林.盘型件双面辗压过程的数值模拟研究[J].锻压装备与制造技术，2006，41(6) ：87-90.Li T, Jin Q L. A study on numerical simulation of double-sided roll forming processes of discal parts[J]. China Metal-forming Equipment & Manufacturing Technology, 2006, 41(6):87-90.
［3］金泉林.盘型件辗压成形载荷的理论分析[J].锻压技术，2007，32(1)：39-43.Jin Q L. Theoretical analysis of rolling forming load for discal parts[J]. Forging & Stamping Technology, 2007,32(1):39-43.
［4］李彤，金泉林，刘晓飞.成形复杂盘型件时辗压工具运动轨迹的研究[J].锻压技术，2008，33(5)：76-81.Li T, Jin Q L, Liu X F. Experimental study on roller feed route of double-sided roll forming of disc parts with complex profile[J]. Forging & Stamping Technology,2008,33(5):76-81.
［5］李彤.盘型件双面辗压成型工艺研究[D].北京：机械科学研究总院，2006.Li T. A study on Technology of Double-sided Roll Forming of Discal Parts
［D］. Beijing:China Academy of Machinery Science & Technology,2006.
［6］李彤，金泉林，刘晓飞.盘型件双面辗压成形过程中打滑缺陷的实验研究[J].塑性工程学报，2009，16(1)：106-109.Li T, Jin Q L, Liu X F. A study on skidding between roller and disk during double-sided roll forming of discal parts[J]. Journal of Plasticity Engineering, 2009, 16(1):106-109.
［7］李彤，刘晓飞，金泉林.盘型件宽槽双面辗压的实验研究[J].塑性工程学报，2007，14（4）：96-100.Li T, Liu X F, Jin Q L. An experiment study on double-sided roll forming of wide groove of discal parts[J]. Journal of Plasticity Engineering, 2007, 14(4): 96-100.
［8］金泉林，刘晓飞.铝合金盘型件等温辗压过程中晶粒尺寸演化的数值模拟与实验验证[J].航空学报，2012，33(2)：335-346.Jin Q L, Liu X F. Numerical stimulation and experimental validation of grain size evolution during double-sided isothermal roll forming for aluminum alloy discal parts[J]. Acta Aeronautica et Astronautica, 2012, 33(2):335-346.
［9］《有色金属及其热处理》编写组.有色金属及其热处理[M].北京：国防工业出版，1981.Editorial Committee of Non-Ferrous Metals and Heat Treatment. Non-Ferrous Metals and Heat Treatment[M]. Beijing: Defence Industry Publishing,1981.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】