汽车板厚度对拉延筋部位摩擦系数测量的影响

英文标题：Influence of auto sheets thickness on measurement of frictional coefficient in draw bead region

作者：李川海

单位：宝钢集团有限公司

分类号：TG386.3

出版年,卷(期):页码：2013,38(1):53-56

摘要：

采用拉延筋模拟试验机测试了板材厚度对摩擦系数测量值的影响，并提出了摩擦系数的修正方法。试验结果表明，板材厚度将使固定拉延筋试样在成形过程中承受不同的变形力，进而影响到最终的摩擦系数值。利用拉延筋模拟试验机进行摩擦系数的测定应该剔除该部分变形力的影响，并且指出相近厚度板材之间的摩擦系数比较更具有现实意义。

Depending on the Draw Bead Simulator (DBS) tester, the influence of autosheets thickness on the frictional coefficient measurement was analyzed. The modified method to the formula was also suggested. The experimental result shows that the autosheets thickness makes the fixed draw bead specimens undertake different deforming force during forming process which influences the final coefficient of friction. It is better to remove such deforming force to test the coefficient of friction using DBS tester, and the comparison of the coefficient of friction between similar thickness sheets is more realistic in practice.

基金项目：

参考文献：

［1］王东哲，张永清，何丹农，等. 大型板材拉深成形的摩擦特征[J]. 金属学报，2001, 7（37）：723-726.
［2］张伟，李志刚，郭正华. 铝合金温成形过程中拉深筋处摩擦的测量[J]. 锻压技术，2007, 32（4）：98-101.
［3］徐树成，王先进. 板成形中摩擦因数测定方法[J]. 钢铁，2001, 36（2）：37-40.
［4］Nine H D. Draw bead force in sheet metal forming [A]. Mechanics of Sheet Metal Forming[C]. New York: Plenum Press，1978.
［5］Sanchez L R. Characterization of a measurement system for reproducible friction testing on sheet metal under plane strain[J]. Tribology International, 1999, 32: 575-586.
［6］李东升，胡世光，黄小明. 拉延成形中拉延筋的摩擦分析[J]. 金属成形工艺，1994, 12（3）：119-122.
［7］李川海，蒋浩民，陈新民,等. 润滑条件对拉延筋钢板表面摩擦系数的影响[J]. 锻压技术，2004, 28（3）：66-68.
［8］Figueiredo L, Ramalho A, Oliveira M C, et al. Experimental study of friction in sheet metal forming[J]. Wear, 2011,271:1651-1657.
［9］李川海. 汽车钢板摩擦行为研究[D]. 上海：同济大学，2007.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】