普通B级船用开平板与中板性能的对比研究

英文标题：Research on properties comparison of B opened plate and middle thickness plate

作者：袁志学董中奇陈敏崔伊滨吴瑾马水明

关键词：船板钢抗拉强度屈服强度伸长率

分类号：TG335

出版年,卷(期):页码：2012,37(6):108-112

摘要：

通过对新工艺下B级船用开平板与传统B级船用中板厚度规格为[10,12] mm, [14,16]mm, [18,20]mm,[22,24]mm 4个组距的抗拉强度、屈服强度、拉伸性能和残余应力等力学性能进行比较分析，获得一系列试验结果。试验结果表明：B级开平板的纵横向抗拉强度与屈服强度指标均优于同等规格的B级中板；B级开平板纵向的伸长率高于横向的伸长率。纵横向力学性能的差异可能是由于纵横向变形程度不同造成的。

The mechanical properties about tensile strength，yield strength，tensile property and residual stress were investigated compared B opened plate using new technology with middle thickness plates using conventional method under thickness standard for [10, 12] mm, [14, 16] mm, [18, 20] mm, [22, 24] mm.The results show that the tensile strength and yield strength of B opened plates are better than the B plate, the longitudinal of B opened plate has an advantage over its longitudinal. The different mechanical properties may be made from the deformation variance of B opened plate in the transverse and the longitudinal.

基金项目：

引进人才科研启动基金项目资助（BZ1001）

参考文献：

［1］ Zhao Y T, Shang C J, Yang S W.The metastable austenite transformation in Mo-Nb-B low carbon steel [J].Materials Science and Engineeting A, 2006,433:169-174.
［2］刘阳春, 徐彬, 武军宽, 等. 首钢船板钢热轧板卷的生产和使用[J]. 钢铁研究学报, 2011, 23 (1): 58-66.
［3］徐党委, 苏晓峰, 夏志升, 等.普通船板B级/DH36的成分优化[J].特钢技术, 2009, 15(3) : 22-24.
［4］杨玉, 叶其斌, 敖列哥, 等.控轧控冷工艺对B级船板钢组织与性能的影响[J]. 金属热处理, 2011, 36 (12) : 16-19.
［5］Imai S. Recent progress and future trends for shipbuilding steel [J]. Welding International, 2008, 22 (11): 755-761.
［6］洪霞, 余驰斌, 叶传龙, 等.热连轧生产船板钢E36静态再结晶行为研究[J]. 钢铁研究, 2011, 39 (4) : 24-26.
［7］王涛, 闫洪. 船板钢E36轧后控冷工艺的制定[J]. 锻压技术, 2008, 33 (1) : 47-49.
［8］高秀华, 邱春林, 杜林秀. 轧制工艺对EH36船板钢显微组织和力学性能的影响[J]. 机械工程材料, 2010, 34 (5): 5-7.
［9］温永红, 唐荻, 武会宾, 等. B级船板钢形变断裂过程的原位研究[J]. 钢铁研究学报, 2009, (5): 15-17.
［10］于守巍，孙群，温荣宇，等.高强船板钢氮含量控制[J]. 鞍钢技术, 2011, 370 (4): 51-54.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】