锻压技术

高铬钢摩擦磨损性能研究

英文标题：Investigation on friction and wear properties of high-chromium steel

作者：黄晓明

单位：云南机电职业技术学院

分类号：TG76

出版年,卷(期):页码：2012,37(5):122-125

摘要：

对含碳1.4wt.% 和含铬15wt.%的Fe\|C\|Cr合金进行退火处理。借助光学显微镜、扫描电镜、XRD对试样微观组织进行观察，通过MMU\|5G型屏显式材料端面摩擦磨损试验机对其磨损性能进行研究。结果表明，在铸造条件下，基材高铬钢组织由初生奥氏体枝晶和(Fe, Cr)7C3、(Fe, Cr)23C6合金碳化物组成。在定转速情况下，随载荷逐渐增大，滑动摩擦系数均不断下降，在载荷较小时其下降幅度较明显，随载荷增大，下降幅度变化趋于平缓。

Fe-C-Cr alloys with 1.4wt.% Carbon and 15wt.% chromium content were annealed. OM, SEM, and XRD were used to analyze the MMG\|5 friction and wear experiment results. It was revealed that as-cast high-chromium steel was composed of primary austenite dendrites and (Fe,Cr)7C3, (Fe,Cr)23C6 carbides. In the condition of constant speed, the friction coefficient kept reducing as the load increasing. Moreover, the decreasing trend seemed to be obvious in the low load. While in the high load, it seemed gentle.

基金项目：

参考文献：

［1］Kambasas K, Tsakiropoilos P. Solidification of high\|Cr white cast iron WC particle reinforced composites[J].Materials Science and Engineering: A，2005，A413414：538-544.
［2］胡正飞,杨振国.高铬耐热钢的发展及其应用[J].钢铁研究学报,2003,15(3):60-65.
［3］王书智.提高穿孔机导板的使用寿命[J].鞍钢技术,1987,(10):25-27.
［4］胡胜.高性能轧辊用高铬钢的热处理工艺优化及组织性能研究[D].湖北：武汉理工大学, 2007.
［5］刘家浚.材料磨损原理及其耐磨性[M].北京:清华大学出版社,2003.
［6］孙德明,许崇海,刘立红,等. Al2O3/Cr3C2/Ti(C,N)复合材料摩擦磨损性能研究[J].人工晶体学报,2008,37(5):30-33.
［7］熊博文,张军,吴振卿.载荷对高铬铸铁磨料磨损的影响[J].热加工工艺:铸锻版,2006,35(5):5-7.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】