HPb59-1黄铜热压缩变形流动应力方程的构建及应用

英文标题：Constitutive equation of HPb59-1 brass during hot compression and its application

作者：肖艳红郭成

单位：西安交通大学

分类号：TG376.2

出版年,卷(期):页码：2012,37(3):127-132

摘要：

通过热压缩实验对HPb59-1黄铜在温度为650～800℃和应变速率为0.1～10s-1下的高温变形行为进行了研究，其真应力真应变曲线表明：流动应力随着应变速率的降低和温度的升高而降低。通过回归拟合实验数据建立了HPb59-1黄铜高温变形流动应力方程，并进行验证。将建立的流动应力方程嵌入Deform\|3D，并对某方法兰件的热挤压成形过程进行数值模拟，研究了该零件热挤压成形规律。最后通过工程实践验证了本研究的有效性，为工程应用提供一定的参考。

The high-temperature deformation behavior of HPb59-1 brass was investigated by isothermal compression tests in the temperature range of 650800 ℃ and the strain rate range of 0.1-10s-1. The true stess-true strain curves show that the stress level decreases with increasing of temperature and decreasing of strain rate. The constitutive equation of HPb59-1 brass was proposed by means of fitting the experimental data and verified. Then, the hot extrusion process of a part with square flange was analyzed using Deform-3D and the forming laws were obtained. Finally, the validity of this research results were proved by practice, which provided some references for engineering application.

基金项目：

参考文献：

［1］邓予生.HPb59-1带断裂的原因分析及措施[J].甘肃冶金，2010,32(2)：110-112.
［2］郭小艳，肖艳红.超高强度铝合金7A04高温流变行为的研究[J].锻压技术，2011,36(4):138-142.
［3］Liu J, Cui Z S, Li C X. Modelling of flow stress characterizing dynamic recrystallization for magnesium alloy AZ31B [J]. Comput Mater Sci., 2008, 41:375-382.
［4］张小刚，潘清林，梁文杰，等. 01570铝合金热压缩变形的流变应力本构方程[J].锻压技术，2009,34(1):139-142.
［5］Lin Y C, Chen X M. A critical review of experimental results and constitutive descriptions for metals and alloys in hot working[J]. Mater. Des., 2011, 32: 1733-1759.
［6］Xiao Y H, Guo C. Constitutive modeling for high temperature behavior of 1Cr12Ni3Mo2VNbN martensitic steel [J]. Mater. Sci. Eng. A, 2011, 528:5081-5087.
［7］张红钢，张辉，彭大署.KFC铜合金热压缩变形流变应力[J].热加工工艺，2004, (1):21-24.
［8］周晓华，柳瑞清.高温下几种铜合金流动应力的研究[J].有色金属加工，2003，32(1)：21-23.
［9］Xiao Y H, Guo C. Constitutive modeling of hot deformation behavior of H62 brass[J]. Mater. Sci. Eng. A, 2011, 528:6510-6518.
［10］Sellars C M, Mctegart W J. On the mechanism of hot deformation[J]. Membr. Sci. Rev. Metall, 1966, 63:731-746.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】