316LN不锈钢锻造开裂锻件组织与断口分析

英文标题：Analysis of forging structure and fracture for 316LN stainless steel forging crack

作者：张义帅张秀芝田香菊郑晓华刘培培

单位：洛阳船舶材料研究所太原科技大学

关键词：316LN 锻造非金属夹杂物裂纹萌生断口形貌

分类号：TG316.1

出版年,卷(期):页码：2011,36(6):1-3

摘要：

针对核电主管道用钢316LN在锻造过程中开裂的现象，借助于金相显微镜（OA）、扫描电镜（SEM）以及能谱仪（EDS）对开裂锻件常温组织以及拉伸断口进行分析。结果表明：脆性氧化铝的大量存在加大了316LN在锻造过程中开裂的倾向。

According to the cracking phenomenon in the forging process of 316LN steel for nuclear power main pipe, with the help of metalloscope(OA), scanning electron microscope(SEM) and energy disperse spectroscopy(EDS), the structure in ordinary temperature and tensile fracture of cracked forging were analyzed.The result shows that the existence of brittle alumina increases the tendency of cracking in 316LN forging process.

基金项目：

“高档数控机床与基础制造装备”科技重大专项（2009ZX04014-062）

参考文献：

[1]Byun T S,Hashimoto N, Farrell K. Temperature dependence of strain hardening and plastic instability behaviors in austenitic stainless steels[J]. Acta Materialia, 2004,(52):3889-3899.

[2]Songtao Wang , Ke Yang, Yiyin Shan,et al. Plastic deformation and fracture behaviors of nitrogen-alloyed austenitic stainless steels[J]. Materials Science and Engineering: A,2008,(490):95-104.

[3]宋永康，刘志颖，郑建能，等.第三代AP1000核电主管道的研制[J].大型铸锻件，2011,（1）：14.

[4]毕晓勤，李金山，耿兴国，等.定向凝固Cu-Cr自生复合材料的组织与断口分析[J].材料热处理学报,2004,3(25):34-37.

[5]胡在矶.加载方式对铸铁断口形貌的影响[J].现代铸铁,2002，(2):58-62.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】