锻压技术

20CrMnTi高温塑性变形行为研究

英文标题：Research on plastic deformation behavior of 20CrMnTi at high temperature

作者：马璟皇涛陈拂晓

单位：河南科技大学

分类号：TG142

出版年,卷(期):页码：2011,36(5):132-136

摘要：

通过在Gleeble-1500热模拟试验机上对20CrMnTi进行压缩试验，然后将压缩后的试样放在扫描电镜下进行组织观察，进而分析了20CrMnTi在高温塑性变形时变形速率和变形温度对其变形抗力以及微观组织的影响，得到了变形抗力和微观组织随变形速率和变形温度而变化的规律，并且建立了其应力应变模型。为20CrMnTi塑性加工时工艺参数的优化提供了可靠的试验数据参考。

Compression test for 20CrMnTi was carried out on hot simulator Gleeble-1500. And the microstructure of the compressed samples was observed by scanning electron microscope. Then the effect of deformation rate and temperature on deformation resistance and microstructure of 20CrMnTi were analysed when it came into plastic deformation at high temperature and the change rules of deformation resistance and microstructure along with deformation rate and temperature were obtained. And stress\|strain model was built. It will provide the reliable reference for the process parameters of hot plastic forming of 20CrMnTi.

基金项目：

参考文献：

[1]中国机械工程学会锻压学会. 锻压手册：锻造[M].北京：机械工业出版社，2002.

[2]皇涛.螺旋伞齿轮精锻工艺及数值模拟研究[D]. 洛阳：河南科技大学，2010.

[3]许勇顺，刘建韬，聂明，等.金属热变形应力应变曲线数学模型的应用与研究[J].应用科学学报，1997,15（4）：379-384.

[4]高威，鞠传华，庞志忠.高强钢变形抗力实验研究[J].重庆科技学院学报:自然科学版，2010,12（6）：144-146.

[5]杨慧，李振红，张质良. 20CrMnTi钢的温热变形行为及其数学建模[J].上海交通大学学报，2005,39（11）:1799-1802.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】