热处理工艺对6061铝合金筒形件旋压过程及其性能影响

英文标题：Influence of heat treatment on spinning process and properties for 6061 aluminum alloy tube

作者：周宇静程秀全夏琴香

分类号：TG306

出版年,卷(期):页码：2011,36(3):54-57

摘要：

为满足某6061铝合金筒形件产品较高的形状、尺寸精度及机械性能要求，对热挤压态6061铝合金管坯件旋前不同热处理工艺规范（退火、固溶、不完全退火和半固溶）进行了分析比较，研究获得不同热处理工艺规范对旋压成形过程及其性能的影响规律。结果表明，对热挤压态6061铝合金管坯件而言，在旋压成形前进行半固溶处理（即将管坯加热到460℃，保温30 min，水冷）, 可确保旋压过程变形稳定，并使经旋压后产品的抗拉强度满足不低于245 MPa的要求。

To meet the requirement of the high shape, dimensional accuracy and mechanical properties of the 6061 aluminum alloy thin-walled tubular part, the different heat treatments, such as the anneal，solution，incomplete annealing and half solution, of the 6061 aluminum alloy hot extrusion tubes before spinning were analyzed. The influence of the heat treatment on the spinning process and the mechanical properties of the spun part were obtained. The results show that for the 6061 aluminum alloy hot extrusion tube, the spinning process proceeds smoothly and the tensile mechanical property of spun part is no less than 245 MPa through the half solution heat treatment (heating to 460℃, insulation 30 min, water-cooling）before spinning.

基金项目：

国家自然科学基金资助项目（51075153）；广东省自然科学基金资助项目（10151040301000000）

参考文献：

［1］夏琴香.冲压成形工艺及模具设计[M].广州：华南理工大学出版社，2004.
［2］喻林.筒形件强力旋压工艺参数优化设计及试验研究[D].哈尔滨：哈尔滨工业大学，2004.
［3］夏琴香，张帅斌，吴小瑜，等.锥形件单道次拉深旋压成形的数值模拟及试验研究[J].锻压技术，2010，35（1）：44-48.
［4］程秀全，刘晓婷.航空工程材料[M].北京：国防工业出版社，2010.
［5］赵云豪，李彦利.旋压技术与应用[M].北京：机械工业出版社，2007.
［6］李成功，傅恒志，于翘，等.航空航天材料[M].北京：国防工业出版社，2002.
［7］王成和，刘克璋.旋压技术[M].北京：机械工业出版社, 1987.
［8］张艳秋，江树勇，孙金凤，等.薄壁筒形件多道次滚珠旋压成形机理研究[J].锻压技术，2010，35（2）：55-58.
［9］王祝堂，田荣璋.铝合金及其加工手册[M].长沙：中南工业大学出版社，2000.
［10］吴凤照，张忠诚，夏琴香.带双侧异形凹槽铝合金壳体成形工艺研究[J].轻合金加工技术，2002，30（12）：35-38.
［11］宋微，张燕飞，刘金诚.热处理工艺对6082铝合金挤压棒材组织和力学性能的影响[J].铝加工，2010，196（5）：42-46.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】