TZM合金轧制变形抗力研究及组织分析

英文标题：Study on rolling deformation resistance of TZM alloy and microstructure analysis

分类号：TG146.4

出版年,卷(期):页码：2011,36(2):107-111

摘要：

利用Gleeble-1500热模拟机对TZM粉末冶金板坯进行轧制热模拟研究。在温度为1150～1300 ℃，变形量为50％，变形速率分别为1,3,5 s-1的试验方案下，采用10 mm×15 mm×20 mm矩形试样，研究了TZM合金板坯的轧制变形抗力与变形温度、变形程度和变形速率之间的关系。结果表明：TZM合金轧制变形抗力随变形温度升高而降低；随着应变速率、变形程度的增大而增大。变形前后的组织分析表明：随着变形量的增加，金相组织微观空洞消失，致密度增大；随变形速率的增大，组织被拉长，晶粒大小趋于均匀化。

Thermal simulation on rolling of TZM alloy slab produced by PM was researched using Gleeble-1500 thermal\|mechanical simulator. The testing programs were performed using rectangular sample with the size of 10 mm×15 mm×20 mm at 11501300 ℃ , the deformation degree of 50％ and the deformation rate at 1,3,5 s-1 respectively. The relationship between rolling parameter (deformation temperature, deformation degree and deformation rate) and deformation resistance of TZM alloy slab were researched. The results indicate that rolling deformation resistance is decreased with the increasing of the temperature, and increased with the increasing of the rate of deformation and deformation degree. Meanwhile, microstructure before and after deformed was analyzed combining with rolling parameters. The analysis shows that the cavities located in metallographic structure are disappeared and the density is increased with the increasing of deformation degree. The texture is elongated and the grain size is evened out with the increasing of the rate of deformation.

基金项目：

国家自然科学基金资助项目（50972039）

参考文献：

［1］Fan Jinglian, Lu Mingyuan, Cheng Huichao,et al. Effect of alloying elements Ti, Zr on the property and microstructure of molybdenum[J]. Int. Journal of Refractory Metals & Hard Materials,2009,(27):78-82.
［2］王敬生. TZM合金板、棒材的研制和应用[J].中国钼业,2007,31(2):44-47.
［3］田家敏,刘拼拼,范景莲，等.钼合金化的研究现状[J].中国钨业,2008,23(4):27-29.
［4］陈程,尹海清,曲选辉. 钼变形抗力的研究[J].稀有金属材料与工程,2007,36(7):1237-1240.
［5］张菊平. 稀土钼塑性加工力学分析[J].中国钼业,2008,32(5):45-47.
［6］陈程,尹海清,曲选辉. TZM钼合金制备技术及研究进展[J].中国钼业,2008,32(6):40-43.
［7］李银华,刘平,贾淑果. 铜合金热变形行为研究[J].金属热处理,2008,33(8):29-32.
［8］寇琳媛,金能萍,张辉. 7150铝合金高温热压缩变形流变应力行为[J].中国有色金属学报,2010,20 (1):43-48.
［9］肖松涛,周廉,王国栋. 钨塑性变形抗力数学模型的研究[J].稀有金属快报,2004,(11):26-28.
［10］梁海成,崔建忠. AZ80镁合金高温热变形流变应力研究[J].锻压技术,2009,34(2):113-116.
［11］Majumdar S, Kapoor R, Raveendra S,et al. A study of hot deformation behavior and microstructural characterization of Mo-TZM alloy [J]. Journal of Nuclear Materials, 2009, 385: 545-551.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】