摘要：
|
|
研究了半固态SiCp/AZ61复合材料在不同变形温度、应变速率、SiCp体积分数和变形程度下的微观组织演变。结果表明,在半固态压缩条件下,在压缩变形过程中随着温度的提高,试样的内摩擦系数减小,使得固相颗粒或者聚集体发生滑动和转动的可能性增加。随应变速率的减小,低应变速率下微观组织中的液相分布在基体周围。随着变形程度的增加,晶粒平均尺寸显著减小。
|
|
Microstructure evolution of semi-solid SiCp/AZ61 composites with different deformation temperatures,strain rates,volume fractions of SiCp and deformation degree during compression process was investigated.The results show that friction coefficient is decreased and the possibility of solid particles or aggregates slipping and rotating will increase with the temperature increase.The liquid phase during low strain rate distributes around the matrix with the strain rate decrease.The grain size decreases obviously with the deformation increase.
|
|
基金项目：
|
|
国家自然科学基金资助项目(50765005);;
江西省自然科学基金资助项目(2007GZC1826);;
江西省教育厅资助项目(GJJ09011)
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]谢水生,黄声宏.半固态金属加工技术及其应用[M].北京:冶金工业出版社,1999.
[2]张发云,闫洪,陈国香,等.SiCP/AZ61镁基复合材料制备工艺和性能的研究[J].铸造,2007,56(6):611-614.
[3]王建金.SiC_p/AZ61复合材料触变塑性成形本构关系研究[D].南昌:南昌大学,2008.
[4]薛勇,张治民,郎利辉,等.AZ91D镁合金高温压缩变形行为[J].锻压技术,2009,34(1):135-138.
[5]罗守靖,祖丽君,杜之明,等.SiC颗粒对SiCp/2024复合材料半固态下压缩行为的影响[J].特种铸造及有色合金,2001,(S1):145-147.
[6]Yan H,Zhou B F.Thixotropic deformation behavior of semi-solid AZ61 magnesium alloy during compression process[J].Materials Science and Engineering:B,2006,132:179-182.
[7]黄维超,卢雅琳,江海涛,等.Al-4Cu-Mg合金半固态压缩过程中的微观组织演变[J].特种铸造及有色合金,2004,(6):8-10.
[8]杨雄飞,康永林,宋仁伯,等.60Si2Mn半固态压缩变形组织演变[J].中国有色金属学报,2000,10(1):120-125.
[9]赵祖德,程远胜,朱世凤,等.Al/Al2O3复合材料的伪半固态压缩变形力学行为[J].材料研究报,2007,21(3):240-244.
|
|
服务与反馈：
|
|
【本网站尚未开通全文下载服务】【加入收藏】
|
|
|
|