摘要：
|
|
对锆合金的热轧工艺进行了研究,采用包覆外套隔氧保护以及多道次、小压下率对合金进行热轧。对3组试样分别采用铜皮包覆,钢套普通焊合包裹,钢套真空电子束焊合包裹等隔氧保护措施,并对轧制后试样的表面氧化状况以及显微组织进行了比较和分析。研究结果表明,只要选用合适的工艺条件,就可以成功防止锆合金在热轧过程中的氧化问题,并且可将锆合金顺利轧薄至1.0 mm左右的板材;热轧后型材显微组织均匀、结构致密,无任何裂纹以及开裂现象,轧制质量好,热轧成材率高。
|
|
The hot rolling process for Zr-alloys was investigated.Cladding outer cover oxygen partition protection,multi working passes and lower rolling rate were used to roll the alloys.Three different ways including copper cover,seam of steel bushing,vacuum seam of steel bushing were respectively applied to three groups of alloys to avoid Zr-alloy's oxidation.Microstructure and mechanical properties after hot rolling were compared and analyzed.The results show that choosing appropriate process technique can successfully avoid oxidation and the alloy's thickness can get to 1.0 mm.After hot rolling,the Zr-alloys exhibit fine and uniform microstructure and good mechanical properties.
|
|
基金项目：
|
|
核燃料及国家重点实验室基金资助项目(5148104105SC0101)
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]陈彬,林栋墚,曾小勤,等.AZ31镁合金大压下率轧制的研究[J].锻压技术,2006,31(3):1 3.
[2]蔡薇,柳瑞清,王晓娟,等.C194合金加工工艺与性能研究[J].锻压技术,2006,31(4):24 26.
[3]彭倩,刘彦章,赵文金,等.热轧温度对N18新锆合金板材织构的影响[J].核动力工程,2005,26(1):65 68.
[4]范洪远,应诗浩,黄新泉,等.铌含量对锆合金组织和耐蚀性的影响[J].材料导报,2005,19(4):443 445.
[5]Jeong Min Kim,Yong Hwan Jeong,Youn Ho Jung.Corre-lation of heat treatment and corrosion behavior of Zr-Nb-Sn-Fe-Cu alloys[J].Journal of Material Proccessing Technolo-gy,2000,5(2):145 149.
[6]Deschamps A,Bre chet Y.Influence of quench and heatingrates on the ageing response of an Al-Zn-Mg-(Zr)alloy[J].Materials Science and Engineering,1998,A(251):200207.
|
|
服务与反馈：
|
|
【本网站尚未开通全文下载服务】【加入收藏】
|
|
|
|