对钻头套零件实施冲裁加工的工艺性进行分析,研究凸模的选材、结构设计和强化处理方法。通过选用GCr15钢制作凸模,并在预先热处理回火时,适当提高回火温度,控制硬度值在HRC54左右,凸模刃口再经激光表面强化处理,得到较高硬度的表面硬化层的同时,保证凸模心部有良好的韧性。试验结果表明:这种方法有利于提高凸模的抗冲击疲劳性能,延长模具使用寿命。因此,冲裁加工钻头套零件,只要措施得当是完全可行的。
|
|
The technique of dill socket parts in punch processing was analyzed.Material selection,structure design and intensity treatment of punch were studied.The punch was made by GCr15 material and the tempering temperature was properly increased during the preheat treatment procedure.The hardness of the die could be controlled around 54HRC.The blade of the punch was processed by laser surface-hardened treatment.Not only the better hardness of the surface was got,but also the better toughness in the punch core part was ensured.The results show that the anit-impact fatigue property of the punch is improved and the life of the punch is prolonged.Hence,it is feasible to machine the punch for processing the drill socket part with proper measures.
|
|
基金项目：
|
|
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]王秀凤,万良辉.冷冲压模具设计与制造[M].北京:北京航空航天大学出版社,2004.
[2]严寿康.冷压工艺及冲模设计[M].北京:国防工业出版社,1993.164 165.
[3]彭成允,邓明.厚板小孔(窄槽)冲裁模具寿命有关问题探讨[J].锻压技术,2000,25(6):50 53.
[4]于永泅,齐民.机械工程材料[M].大连:大连理工大学出版社,2006.
[5]欧阳八生,樊湘芳,娄燕.行星轮轴承载表面激光强化[J].金属热处理,2004,29(7):78 80.
|
|
服务与反馈：
|
|
【本网站尚未开通全文下载服务】【加入收藏】
|
|
|
|