锻压技术

B180H1钢板成形性能研究

英文标题：Research on the formability of steel sheet B180H1

作者：武晋毕大森张建彭本栋

单位：天津理工大学材料科学与工程学院天津理工大学材料科学与工程学院天津理工大学材料科学与工程学院天津理工大学材料科学与工程学院天津300191 天津300191 天津300191 天津300191

分类号：TG115

出版年,卷(期):页码：2007,32(6):64-67

摘要：

高强度烘烤强化(BH)钢是汽车覆盖件用的高强度钢板。本文通过试验对汽车用高强度钢板B180H1的力学性能、成形性能、烘烤硬化性能和抗凹陷性能进行了全面的研究,并与DC04钢板的各项性能进行了比较。使用NADDRG模型对B180H1钢的成形极限进行了预测。试验结果表明,与DC04钢相比,B180H1钢的屈服强度提高了40.8%,抗拉强度提高了18.4%,延伸率下降了15.6%,且B180H1的塑性应变比和应变硬化指数也高于DC04钢。这说明B180H1的力学性能优于DC04,成形性能不低于DC04,且B180H1的烘烤硬化性能及抗凹陷性能方面均优于DC04。

High strength haked-hardening(BH)steel is a high strength steel for auto-panel.The mechanical property, forming ability,baked-hardening and dent resistance properties of high strength steel B180H1 were studied by experi- ments compared with those of steel DC04,and theoretical research on predicting the forming limit of steel B180H1 by the NADDRG model was made.The experimental results reveal that the yield strength of steel B180H1 is about 40.8% higher than that of DC04,and the break strength increases by 18.4%,while the elongation decreases by 15.6%.The plastic strain ratio and strain hardening exponent of steel B180H1 are superior to those of DC04.The re- suits show that mechanical property of high strength steel B180H1 is better than that of DC04,while forming ability of B180H1 is not lower than that of DC04.The baked-hardening and dent resistance properties of steel B180H1 are better than those of DC04.

基金项目：

天津市科技支撑计划项目，(07ZCKFGX02400)

参考文献：

[1]Takehide Scnuma.Physical metallurgy of modem Hish strength steel sheets[J].ISIJ International,2001,41(6): 520-532.
[2]申昱，于沪平，阮雪榆．材料塑性与几何尺寸关系研究[J]．锻压技术，2006，31(6)，64-67．
[3]龚红英，李名尧，黄金湘，等．材料力学性能参数对ST07Zn车用钢板拉深成形特性的影响[J]．锻压技术，2007，32 (3)：26-29．
[4]李东升，李雪峰，周贤宾．汽车板材烘烤硬化特性的研究[J]．金属成形工艺，2001，19(2)：14-17．
[5]康永林，孙建林．高强度薄钢板研究的新进展及其在汽车上的应用[J]．钢铁，2002，37(5)：65-70．
[6]Fang X F,Dahl W.Influence of the microstructure on strain hardening of steels[J].Materials Research and Advanced Techniques,1995,86(1):41-48.
[7]Gusek C O,Bleck W,Dahl W.Modeling of sheet metal tes- ting[J].Computational Materials Science,1996,7(1): 173-180.
[8]余海燕，陈关龙，李淑慧．TRIP高强度钢板成形极限的实验研究[J]．中国机械工程，2004，15(23)：2158-2161．
[9]江海涛，康永林，王全礼，等．高强度汽车板的烘烤硬化特性[J]．钢铁研究，2006，34(1)：54-57．

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】