摘要：
|
|
对汽车用轴类部件的热锻模具进行失效分析。通过能谱分析、扫描电镜、显微硬度测定等多种检测手段,分析了热锻模具的失效机理。结果表明,失效热锻模具钢工作面表层材料氧化,表面合金元素重新分布,局部合金元素降低,导致材料局部硬度、耐磨性及热强度下降,这是产生初始裂纹及蚀点的主要原因,初始破损的进一步扩展导致了模具的最终失效。
|
|
The failure mechanism was analyzed on automobile hot-forging dies by means of EDS,micro-hardness and metallographic examination.The results show that surface oxidation and dispersing of alloying elements in surface layer lead to the reduction of hardness,wear resistance and hot strength of the steel,which cause the initial surface cracks.Continuous propagation of the cracks results in the final failure of the dies.
|
|
基金项目：
|
|
教育部长江学者与创新团队计划(IRT0720);;
北京市教委科技成果转化与产业化项目资助
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]曾珊琪,丁毅.模具寿命与失效[M].北京:化学工业出版社,2005.
[2]宝志坚.汽车热锻模具的失效机理及延寿技术[D].北京:华北电力大学,2006.
[3]樊东黎,王广生.热处理手册[M].北京:机械工业出版社,2001.
[4]徐滨士.神奇的表面工程[M].北京:清华大学出版社,2000.
[5]Johnson P K,Arana M,Ostolaza M,et al.Crack initiationin a coated and uncoated nickel-base superalloy under TMFconditions[J].Journal of Engineering for Gas Turbines andPower,1998,10:791-795.
[6]刘宗德,安江英,杨昆,等.电爆炸高速喷涂新技术研究[J].爆炸与冲击,2001,(1):17-20.
[7]王彦可,杨永顺,候明,等.轴承保持架温挤压模具失效分析[J].锻压技术,2006,31(1):61-63.
[8]石钟良,蔡莲淑,莫东强,等.气门热精锻模具的正常与异常失效[J].锻压技术,2001,(5):58-60.
|
|
服务与反馈：
|
|
【本网站尚未开通全文下载服务】【加入收藏】
|
|
|
|