塑性变形对AZ31镁合金组织性能的影响研究
|
|
英文标题：Study on influence of plastic deformation on microstructure and properties of AZ31 alloy |
|
作者：张会 冯小明 郭从盛 李雷权 刘自乾 |
|
单位：陕西理工学院材料科学与工程学院 |
|
关键词：塑性变形 极限变形量 晶粒尺寸 |
|
分类号：TG146.22 |
|
出版年,卷(期):页码：2009,34(1):146-148 |
|
摘要：
|
|
由于镁是密排六方结构,只有有限的滑移系,又缺乏有效的强化相,限制了镁合金的工程应用。本文通过不同温度下镁合金的塑性极限变形量来分析镁合金强度和塑性的影响因素。通过实验研究了塑性变形对AZ31合金组织和性能的影响。结果表明,在350℃下镁合金的极限变形量可达到79%,在不同压缩变形下,变形量越大,晶粒越细,分布越均匀。变形量达到70%时,晶粒尺寸基本为2~3μm。
|
|
Magnesium is of six-party row structure,only has a limited slip system,and lacking of an effective strengthening phase,so the application of magnesium alloy is restricted.Based on the different temperatures of magnesium alloy plastic deformation limit of magnesium alloy,the plastic strength of the plastic impact factors were analyzed.Through experiments on the plastic deformation of the alloy AZ31,it is concluded that under 350 ℃,magnesium alloy maximum reduction is up to 77.8%,in different deformations,the bigger deformation,the more fine grain distribution.When the deformation is up to 70%,the basic grain size is of 2-3 μm.
|
|
基金项目：
|
|
陕西理工学院科研项目(SLG0728)
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]王东渠,王文江.轿车用阻燃镁合金的研究[J].材料导报,2000,14(9):43-47.
[2]曹荣昌,柯伟,徐永波,等.Mg合金的最新应用及研究进展[J].金属学报,2001,37(7):43-47.
[3]Kim S,Kim J,Shin D H,et al.Microstructure developmentand segment formation during ECAP ressing of Ti-6Al-4V al-loy[J].Scripta Materialia,2004,50(7):927-930.
[4]余琨,黎文献,王日初.变形镁合金的研究[J].中国有色金属学报,2003,13(2):15-18.
[5]刘英,陈维平,张卫文,等.等通道转角挤压AZ31镁合金的微观结构与性能[J].华南理工大学学报:自然科学版,2004,32(9):3-7.
[6]韩德伟,张建新.金相制备与显示技术[M].长沙:中南大学出版社,2005.
[7]杜忠泽,伍来智,符寒光,等.ECAP变形2J4合金的显微组织演变[J].航空材料学报,2008,28(1):23-29.
|
|
服务与反馈：
|
|
【本网站尚未开通全文下载服务】【加入收藏】
|
|
|
|