高耐蚀型耐候钢S450EW热轧工艺及腐蚀性能
英文标题:Hot rolling process and corrosion properties for high corrosion resistant weathering steel S450EW
作者:张慧菊 李春辉 
单位:厦门工学院 
关键词:S450EW钢 耐候钢 热轧工艺 高耐蚀性能 腐蚀率 
分类号:TG335
出版年,卷(期):页码:2020,45(7):198-202
摘要:

 制定了S450EW高耐蚀型耐候钢的热轧工艺,具体为:加热—粗轧—精轧—层流冷却—卷取,粗轧材料厚度控制值为40 mm,温度控制在(1050±20) ℃范围内,精轧材料厚度控制值为7 mm,温度控制在(870±20) ℃范围内,并对不同热轧工艺的样品进行金相试验及力学性能检测,以确定各工艺参数的设定范围。同时,完成S450EW钢的腐蚀性能验证,将试验钢的轧制成品径线切割为70 mm×50 mm×3.5 mm的板状,并在Fl-65型干湿周期浸润腐蚀试验机内进行试验。结果表明,S450EW钢的两种试验样品的平均腐蚀率分别为1.770和1.839 g·m-2·h,明显小于参比钢Q345试样的平均腐蚀率2.909 g·m-2·h。

 The hot rolling process of high corrosion resistant weathering steel S450EW was made with heating-rough rolling-finishing rolling-laminar cooling-coiling. The thickness control value of rough rolling material was 40 mm with the temperature of (1050±20) ℃, and the thickness control value of finishing rolling material was 7 mm with the temperature of (870±20) ℃. Then, the samples of different hot rolling processes were subjected to metallographic test and mechanical property test to determine the setting range of each process parameter. Meanwhile, the corrosion property verification of S450EW steel was completed, the rolled product of test steel was cut into a plate shape with 70 mm×50 mm×3.5 mm by wire cutting, and the test was made in the FL-65 dry and wet periodic infiltration corrosion testing machine. The results shows that the average corrosion rates of two test samples of S450EW steel are 1.770 and 1.839 g·m-2·h respectively, which is significantly lower than the average corrosion rate of 2.909 g·m-2·h for reference Q345 steel sample.

基金项目:
福建省教育厅中青年教师教育科研项目(JAT160630)
作者简介:
张慧菊(1987-),女,硕士,讲师 E-mail:307787273@qq.com
参考文献:

 [1]冯绍强. 川威SPAH耐候用热轧带钢研制开发[J]. 四川冶金,201133(3)23-27.


 


Feng S Q. SPAH weather research and development of hot rolled strip[J]. Sichuan Metallurgical, 201133(3)23-27.


 


[2]王俊山. 高耐蚀性铁路货车用S450EW钢的研制开发[D].沈阳:东北大学,2014.


 


Wang J S. Research and Development of High Weather S450EW Steel for Railway Freight Wagons[D]. Shenyang: Northeastern University, 2014.


[3]江锐锋, 焦辉. 铁路货车用S450EW高耐蚀型耐候钢工艺性能分析[J].机车车辆工艺,2013,(4)1-4.


Jiang R F, Jiao H. Process performance analysis of S450EW high corrosion resistant weathering steel for railway freight cars[J]. Locomotive and Vehicle Technology, 2013,(4):1-4.


[4]岳重祥, 白晓虹,刘东升,等. 利用TMCP开发F550高强度船板钢的实验研究[J].材料工程,2013(2)7-11, 28.


Yue C X, Bai X H, Liu D S,et al. 550 high strength plate steel for ship building produced by TMCP[J]. Materials Engineering, 2013, (2):7-11, 28.


[5]武凤娟, 程丙贵,刘东升,等. TMCP高强韧F460厚板及焊接接头的组织和性能[J].上海金属,201840(5)21-27.


Wu F J, Cheng B G, Liu D Set al. Microstructure and mechanical properties of welded joint for TMCP processed high strengthtoughness F460 heavy plate[J]. Shanghai Metal, 201840(5):21-27.


[6]刘泽田, 陆斌,惠鑫,等. 薄规格高强船板轧制工艺的研究[J].山东冶金,201436(6)34-35,38.


Liu Z T, Lu B, Hui Xet al. Research on the rolling process of thin plate with high strength[J]. Shandong Metallurgical, 201436(6):34-35,38.


[7]陈斌, 白丽杨,张宇光,等. 卷取温度对IF钢组织性能影响规律[J].中国冶金,201929(8)34-38.


Chen B, Bai L Y, Zhang Y Get al. Effect of coiling temperature on microstructure and properties of IF steel[J]. China Metallurgical, 201929(8):34-38.


[8]张杰. 高强耐候钢的生产工艺与组织性能研究[D]. 唐山:华北理工大学,2018.


Zhang J. Study on the Production Process and Microstructure Properties of High Strength Weathering Resistant Steel[D]. Tangshan: North China University Science and Technology, 2018.


[9]朱阳林, 岳重祥,李慧,等.汽车结构用热轧酸洗板QStE420的开发[J]. 金属热处理,201843(10)50-53.


Zhu Y L, Yue C X, Li Het al. Development of hot rolled and pickled automotive steel QStE420[J]. Metal Heat Treatment, 201843(10):50-53.


[10]TB/T 23751993,铁路用耐候钢周期浸润腐蚀试验方法[S].


TB/T 23751993Test method for cycle infiltration and corrosion of railway weatherresistance steel[S].


[11]吴晓东, 孙霞飞.一种耐候钢耐蚀性能的分析[J]. 热加工工艺,201443(8)69-72.


Wu X D, Sun X F. Analysis on corrosionresistant of weathering steel[J]. Hot Working Process, 201443(8):69-72.


[12]Wang J S, Shi P Y, Liu C J, et al. Corrosion behavior of S450EW lowalloy weathering steel in cyclically alternate corrosion environments[J]. Journal of Iron and Steel Research International, 2015, 22(11):1020-1023.


[13]何博, 张建,胡学文,等.铁道车辆用高耐蚀型耐候钢耐腐蚀性能研究[J]. 安徽冶金科技职业学院学报,201727(4) 1-5,13.


He B, Zhang J, Hu X Wet al. Study on corrosion resistance of high corrosion resistant weathering steels for railway vehicles[J]. Journal of Anhui Metallurgical Science and Technology Vocational College, 201727(4):1-5,13.

服务与反馈:
本网站尚未开通全文下载服务】【加入收藏
《锻压技术》编辑部版权所有

中国机械工业联合会主管 北京机电研究所有限公司 中国机械工程学会塑性工程分会主办
联系地址:北京市海淀区学清路18号 邮编:100083
电话:+86-010-62920652 +86-010-82415085 传真:+86-010-62920652
E-mail: fst@263.net(稿件) dyjsjournal@163.com(广告)
京ICP备09032115号-5