锻压技术

铸造合金CoCrMoW锻造工艺的研究

英文标题：Research on forging process of casting alloy CoCrMoW

分类号：TG141；TG156.1

出版年,卷(期):页码：2017,42(6):12-15

摘要：

通过对CoCrMoW合金电渣锭在两种不同的保温制度下保温后进行两种不同的锻造变形方式开坯锻造，研究了CoCrMoW电渣锭锻造保温温度及锻造变形方式对可锻性的影响。试验研究结果表明：CoCrMoW合金电渣锭在1220 ℃保温1 h后采用整体锻造，锻件的表面质量与内部质量良好；1200 ℃保温2 h后，采用整体锻造，锻件的表面质量良好，但是内部有缺陷产生；CoCrMoW合金电渣锭在1220 ℃保温1 h后锻造变形，电渣锭采用分段锻造时表面出现开裂，采用整体锻造时表面质量与内部质量良好；经过开坯后的小规格坯料再继续开坯或锻成品时，分段锻造与整体锻造均可采用。该合金合理的锻造保温温度为1220～1240 ℃，电渣锭锻造变形方式必须采用整体锻造；小规格锻造方坯变形方式宜采用整体锻造，但也可采用分段锻造。

For CoCrMoW electroslag remelting ingots, the influences of holding temperatures and forging processes on forgeability were studied by forging the casting alloy CoCrMoW electroslag remelting ingots under two different holding temperatures and two different forging processes. The result shows that both surface quality and internal soundness of CoCrMoW electroslag remelting ingots are all right by whole forging at 1220 ℃ for 1 h, while the surface quality is good, but the internal soundness is bad at 1200 ℃ for 1 h. However, the forging deformation occurs after heating at 1220 ℃ for 1 h, and it cracks on the surface by sectional forging. Furthermore, the sectional forging and whole forging can be applied to small standard stock that is opened billet continually or forged after the opened billet, and the holding temperature is 1220-1240 ℃. However, the best deformation model of CoCrMoW electroslag remelting ingots is forged as a whole, and the deformation model of small standard stock can be forged as a whole or forged sectionally.

基金项目：

重庆市新产品创新青年科技人才培养计划项目（cstc2013kjrc-qnrc50005）；重庆市重点产业共性关键技术创新专项项目（cstc2015zdcy-ztzx50002）

代礼斌（1985-），男，硕士，工程师

参考文献：

［1］马秀萍，李超. 铸造过热度和热处理对CoCrMo合金显微组织的影响[J]. 材料工程，2014, (3):66-70.

Ma X P, Li C. Effect of superheat temperature for casting and heat treatment on microstructure of CoCrMo Alloy[J]. Journal of Materials Engineering, 2014, (3):66-70.

［2］Fazira M F, Mohammad M, Roslani N, et al. Low strain rate upset forging of preformed CoCrMo powder alloy for load bearing application: A review [J]. Procedia Engineering, 2013, 68(12):405-410.

［3］王彩梅，周学玉，孙元，等. 航空材料在外科植入物骨关节假体中的应用[J]. 材料工程，2007,（3）：58-61.

Wang C M, Zhou X Y, Sun Y, et al. Application of aviation materials in implants for surgery-joint prosthesis[J]. Journal of Materials Engineering,2007,(3):58-61.

［4］盖学周，饶平根，赵平岩，等. 人工关节材料的研究进展[J]. 材料导报，2006，20（1）：46-49.

Gai X Z, Rao P G, Zhao P Y, et al. Progress in research of artificial joint materials[J]. Materials Review, 2006,20(1):46-49.

［5］张鑫，陈辉，陈凯. 锻造CoCrMo合金关节材料滑动摩擦腐蚀行为[J]. 中国表面工程，2016，29(2):43-48.

Zhang X, Chen H, Chen K. Sliging tribocorrosion behavior of forged CoCrMo alloy for artificial joint materials[J]. China Surface Engineering, 2016, 29(2):43-48.

［6］Chen Y, Li Y, Kurosu S, et al. Effects of microstructures on the sliding behavior of hot-pressed CoCrMo alloys[J]. Wear, 2014, 319(1-2):200-210.

［7］Yamanaka K, Mori M, Kuramoto K, et al. Development of new Co-Cr-W-based biomedical alloys: Effects of microalloying and thermomechanical processing on microstructures and mechanical properties[J]. Materials & Design, 2014,55:987-998.

［8］史胜凤. 医用钴基合金的组织结构及耐腐蚀性能[D]. 杭州：浙江大学，2006.

Si S F. Microstructure and Corrosion Resistance of Medical Cobaltbased Alloys[D]. Hangzhou:Zhejiang University, 2006.

［9］师昌绪，李恒德，周廉,等. 材料科学与工程手册[M]. 北京：化学工业出版社，2004.

Shi C X, Li H D, Zhou L, et al. Materials Science and Engineering Handbook[M]. Beijing: Chemical Industry Press, 2004.

［10］Niinomi M, Narushima T, Nakai M. Advances in metallic biomaterials-processing and applications[J]. Springer Series in Biomaterials Science and Engineering，2015, (4):73-81.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】