锥孔锻件自动化闭式热挤压工艺
英文标题:Automatic closed hot extrusion process of cone hole forging
作者:闫红艳 徐超 王志科 谢谈 郭永强 
单位:北京机电研究所 
关键词:锚套 热挤压 同轴度 磨损 自动化 
分类号:TG316
出版年,卷(期):页码:2017,42(4):109-116
摘要:

针对锚固装置中的锚套典型件,设计了自动化热挤压工艺。试生产中出现锻件质量不稳定和模具寿命太低等问题,导致难以实现自动化生产。质量不稳定的表现是锻件同轴度超差且无规律,模拟分析了预锻同轴度对成形凸模等效应力和偏移量的影响,并通过提高坯料尺寸精度和调整镦粗高度解决了同轴度的问题,使锻件同轴度从最大Φ0.86 mm减小到Φ0.4 mm以内,确保了锻件质量稳定合格。成形凸模失效的表现是磨损,模拟分析了不同材料、润滑系数、凸模长径比对模具磨损量的影响,并通过实验确定:润滑剂采用水基石墨,凸模材料采用3Cr2W8V钢,将模具寿命从1500件提高到10000件以上,可以连续生产20 h以上。最终实现班产不换模具且无废品,达到自动化生产的要求。

For the typical parts of anchor sleeve for anchoring device, an automatic hot extrusion process was designed. The instable forging quality and short die lifetime during the production hindered the realization of automated production. The performance of quality instability was the coaxiality of big tolerance and not regular in the forging. Then, the influences of pre-forging coaxiality on the equivalent stress and offset of forming punch were simulated and analyzed. Therefore, the problem of coaxiality was solved by improving the blank size accuracy and adjusting the upsetting height, and its coaxiality was reduced from Φ0.86 mm to Φ0.4 mm or less to ensure the stable forging quality. However, the forming punch failure displayed the wear, and the influences of different materials, lubrication coefficient and punch length to diameter ratio on the die wear were simulated and analyzed. The experiment results show that the die life is increased from 1500 pieces to 10000 pieces with water-based graphite lubricant and punch material 3Cr2W8V steel, and the continuous production is up to 20 hours at least. Finally, a day without changing dies and defects unqualified forgings can be realized to achieve the requirements of automated production.

基金项目:
国家国际科技合作专项项目(2015DFA51740)
作者简介:
闫红艳(1979-),女,硕士研究生,高级工程师 E-mail:yanhongyan2013@126.com 通讯作者:谢谈(1953-),男,学士,教授级高工 E-mail:xietan@jds.ac.cn
参考文献:

[1]丁伯艮. 爪极闭式挤压数值模拟及工艺实验研究[D].马鞍山:安徽工业大学,2014.


Ding B G. Research on Numerical Simulation and Process Experiment of Claw Pole Die Closed Extrusion[D]. MaanshanAnhui University of Technology2014.


[2]周杰,赵军,安治国. 热挤压模磨损规律及磨损对模具寿命的影响[J]. 中国机械工程,2007, 18(17):2112-2115.


Zhou JZhao JAn Z G. Wear rule and effects on the die service life during hot extrusion[J]. China Mechanical Engineering, 2007, 18(17): 2112-2115.


[3]陈明. 多工位热模锻压力机机身设计与优化[D].南京:南京理工大学,2013.


Chen M. Design and Optimization of Multi-Station Hot Die Forging Press[D]. NanjingNanjing University of Science and Technology2013.


[4]凌艳路,孙国强,蒋鹏.铁路货车中型锻件自动化生产线的设计与应用[J]. 锻压技术,201641(5)151-154.


Ling Y LSun G QJiang P. Design and application on automation production line of medium forging workpiece for railway truck [J]. Forging & Stamping Technology201641(5)151-154.


[5]祁鹏飞. 筒形件热冲压工艺数值模拟及试验研究[D].北京:机械科学研究总院,2013.


Qi P F. Numerical Simulation and Experimental Research on Hot Stamping Process for Barrel-Type Workpiece[D]. BeijingChina Academy of Machinery Science and Technology2013.


[6]谢志平,万博维,张治民,等.大型深孔圆锥形构件省力挤压成形工艺研究[J]. 锻压技术,201540(2)87-92.


Xie Z PWan B WZhang Z Met al. Research on labor-saving extrusion forming process of large deep hole conical workpiece [J]. Forging & Stamping Technology201540(2)87-92.


[7]潘秀秀,杨屹,杨刚,等.工作夹片的锻造工艺数值模拟分析[J]. 锻压技术,201540(3)11-15.


Pan X XYang YYang Get al. Numerical simulation and analysis of forging process for the work clamping piece [J]. Forging & Stamping Technology201540(3)11-15.


[8]任杰, 王强,冀翠斌,等.反挤压筒形件成形力研究[J]. 锻压技术,20154011):122-126.


Ren JWang QJi C Bet al. Study on forming force of cylindrical part in backward extrusion [J]. Forging & Stamping Technology201540(11)122-126.


[9]李振红,黄英娜,张质良. 亚热精密成形过程模具磨损的数值模拟研究[J]. 精密成形工程,2010, 2(2):5-9.


Li Z HHuang Y NZhang Z L. Die wear simulation of semi-hot precision forming process[J]. Netshape Forming Engineering2010, 2(2):5-9.


[10]张明.6061铝合金热挤压过程中的摩擦磨损行为等效表征研究[D].长沙:湖南大学,2014.


Zhang M. Equivalent Characterization of the Friction and Wear Behavior during Hot Extrusion of 6061 Aluminum Alloy[D]. ChangshaHunan University2014.


[11]李宝聚,王兆辉,谭磊,等. 热锻工艺参数对模具磨损影响的有限元分析[J]. 模具工业, 2014, 40(9):6-11.

Li B JWang Z HTan Let al. Finite element analysis of effect of hot forging process parameters on die wear[J]. Die & Mould Industry,2014, 40(9):6-11.

服务与反馈:
本网站尚未开通全文下载服务】【加入收藏
《锻压技术》编辑部版权所有

中国机械工业联合会主管 北京机电研究所有限公司 中国机械工程学会塑性工程分会主办
联系地址:北京市海淀区学清路18号 邮编:100083
电话:+86-010-82415085 传真:+86-010-62920652
E-mail: fst@263.net(稿件) dyjsjournal@163.com(广告)
京ICP备07007000号-9