AZ31B镁合金板热渐进成形的精度研究

英文标题：Study on the accuracy of hot incremental forming for magnesium alloy sheet AZ31B

作者：文怀兴刘桂芳史鹏涛

单位：陕西科技大学

分类号：TG335

出版年,卷(期):页码：2017,42(4):59-62

摘要：

成形精度差是限制单点渐进成形发展的重要因素，针对单点渐进成形技术难以实现对材料高温处理再加工的问题，提出一种基于液体介质加热的单点渐进成形方法，并通过依次提高温度的方法，探索了适合进行AZ31B镁合金板料单点渐进成形的实验温度。同时，研究了在该温度下采用单点渐进成形方法加工AZ31B镁合金方锥件时，成形角对精度的影响。结果表明：液体介质加热的方法对单点渐进成形有效，在加热油温达到200 ℃时能够完成镁合金板料的单点渐进成形过程；方锥成形件的精度影响分两种形式——侧壁鼓凸和棱边回弹，并且随成形角的增大，侧壁鼓凸和棱边回弹的回弹量都减小。

The low precision is a critical factor that obstacles the development of single point incremental forming. For the difficulty of high temperature reprocessing in the single point incremental forming, a single increamental forming method by liquid medium heating was proposed, and the suitable single point incremental forming temperature of magnesium alloy sheet AZ31B was explored by increasing temperature gradually. At the same time, the influence of forming angle on the accuracy was studied for processing pyramidal parts of magnesium alloy AZ31B by the single point incremental forming at this temperature. The results show that this method of liquid medium heating is feasible and can complete the single point incremental forming process for the magnesium alloy sheet at the heating oil temperature of 200 ℃. Furthermore, the influences on the accuracy are from two forms as wall bulge and edge springback, and the wall bulge and edge springback are reduced with the increasing of forming angle.

基金项目：

陕西科技大学科研启动基金项目（BJ10-07）

文怀兴（1957-），男，博士，教授 E-mail：492808529@qq.com 通讯作者：刘桂芳（1994-），女，硕士研究生 E-mail：787219913@qq.com

参考文献：

[1]张津, 章宗和. 镁合金及应用[M].北京:化学工业出版社,2004.

Zhang J, Zhang Z H. Magnesium Alloy and Its Application[M]. Beijing: Chemical Industry Press, 2004.

[2]陈振华. 镁合金[M].北京：化学工业出版社，2004.

Chen Z H. Magnesium Alloy[M]. Beijing: Chemical Industry Press,2004.

[3]张会，冯小明，郭从盛，等．塑性变形对AZ31镁合金组织性能的影响研究[J]．锻压技术，2009,34(1):146-148.

Zhang H, Feng X M, Guo C S, et al. Study on influence of plastic deformation on micro structure and properties of AZ31 alloy [J]. Forging & Stamping Technology,2009,34(1):146-148.

[4]Bruni C C, Forcellese A, Gabrielli F, et al. Effect of temperature, strain rate and fibre orientation on the plastic flow behaviour and formability of AZ31 magnesium alloy [J]. Journal of Materials Processing Technology, 2010, 210(10): 1354-1363.

[5]张青来, 肖富贵,郭海玲,等. 镁合金板材热渐进成形的实验研究[J]. 四川大学学报: 工程科学版,2009, 41(5): 120-125.

Zhang Q L, Xiao F G, Guo H L, et al. Research on incremental forming of AZ31B sheet at elevated temperature[J]. Journal of Sichuan University: Engineering Science Edition,2009, 41(5):120-125.

[6]苏春建, 张鹏, 赵俊敏, 等. AZ31B镁合金无模单点温渐进成形回弹影响因素研究[J]. 锻压技术, 2016, 41(3): 44-47.

Su C J, Zhang P, Zhao J M, et al. Study on the influential factors of springback for magnesium alloy AZ31B in single point warm incremental forming[J]. Forging & Stamping Technology, 2016, 41(3): 44-47.

[7]周六如, 郑志强,罗忠民. 工具转速对AZ31B镁合金圆锥盒摩擦热渐进成形板料温度及成形能力的影响[J]. 锻压技术, 2016, 41(9):31-34.Zhou L R, Zheng Z Q, Luo Z M. Influence of tool speed on sheet temperature and formability of magnesium alloy AZ31B cone box in frictional heat incremental forming[J]. Forging & Stamping Technology, 2016, 41(9): 31-34.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】