基于高强度拼焊板的B柱内板工艺参数研究
英文标题:Research of process parameters on B-pillar inner based on HSSTWB
作者:张双杰 张招 闫华军 韩炳辉 何阳 贾亚飞 
单位:河北科技大学 河北金环模具有限公司 
关键词:B柱内板 高强激光拼焊板 正交试验 回弹补偿 
分类号:TG386.1
出版年,卷(期):页码:2014,39(3):29-33
摘要:

高强度激光拼焊板具有减轻车身重量、节能环保、改善车身安全性能等优点。研究了工艺参数对差厚高强度激光拼焊板B340/590DP成形汽车B柱的影响规律,设定了冲压速度、压边力、模具间隙、摩擦系数4个工艺参数的正交试验方案,利用有限元软件Dynaform对B柱内板成形过程进行模拟,得到关于最小减薄率的最优参数。利用软件中回弹补偿模块进行拉延模具修正,利用优化的工艺参数,进行了工艺试验。试验结果与模拟结果一致,即制件成形良好,焊缝没有破裂,回弹量小于1mm,最小减薄率小于20%。采用有限元方法与工艺试验相结合的方法,减少了修模次数,得到了合格的零件。
 

High-intensity laser welded blanks have the advantage of reducing body weight, saving energy and protecting environment, improving body safety and so on. The effect of process parameters on forming B-pillar of car based on differential high strength steel tailor welded blank (HSSTWB)B340/590DP was researched. The orthogonal experiment scheme of four process parameters was set up, and the process patameters include punching speed, orthogonal program BHF, die clearance and friction coefficient. The forming process of B-pillar panel was simulated using the finite element software Dynaform, and the best parameters which effect minimum rate of thinning were obatained. The correction of drawing die was finished using the springback compensation module, and the process test was made using the optimized process parameters. The test results are consistent with the simulation results, the forming propety of parts is well, the welding line does not rupture, the springback value is less than 1mm and the minimum rate of thinning is less than 20%. When finite element method is integrated with process test, the number of repairing die reduces and qualified parts are obatained.
 

基金项目:
石家庄市科技局重大项目(12108151A)
作者简介:
参考文献:


[1]刘文华, 何天明. 高强度钢在汽车轻量化中的应用[J]. 汽车工艺与材料, 2008, (11): 49-51.Liu Wenhua, He Tianming. High strength steel in automobile lightweight application[J]. Automotive Technology and Materials, 2008, (11): 49-51.
[2]宋燕利,华林.车身覆盖件拼焊板冲压成形技术的研究现状及发展趋势[J]. 中国机械工程, 2011, 22(1): 115-116.Song yanli, Hua lin. Current research status and trends of tailor welded blanks applied in auto body stamping[J]. China   Mechanical Engineering, 2011, 22(1): 115-116.
[3]Heller T, End B, Ehrhardt B, et al. New high strength steels production[J]. Properties & Applications, 1998, 16(3): 25-34.
[4]李贵, 柳玉起, 柯俊逸, 等. 先进高强度钢板DP590回弹试验及数值模拟研究[J]. 锻压技术, 2013, 38(5): 50-55.Li gui, Liu yuqi, Ke Junyi, et al.  Experimental reasearch and numerical simulation of spingback for advanced high strengh steel- DP590[J]. Forging & Stamping Technology, 2013, 38(5): 50-55.
[5]Chen G, Chen X, Shi F. Material and processing modeling of dual phase steel[J]. Front Rails for Crash Ahsss Proceedings, 1998, (7): 161-170.
[6]Shaw J,Watanabe  K,Chen  M. Metal forming characterization and simulation of advanced high strength steels[J]. SAE, 2001, 1(11): 1-10.
[7]邢忠文, 方华松, 徐伟力. 汽车B柱成形仿真与分析[J]. 锻压技术, 2008, 33(2): 27-30.Xing zhongwen, Fang huasong, Xu weili. Simulation and formability analysis of drawing process for car B pillar[J]. Forging & Stamping Technology, 2008, 33(2): 27-30.
[8]张招. 基于高强度薄板的B柱内板回弹分析及成形工艺研究[D]. 石家庄:河北科技大学, 2012.Zhang zhao. Springback Analysis and Drawing Process Research of B-pillar Inner Based on High-strongth Steel[D]. Shijiazhuang:Hebei University of Science and Technology, 2012.
[9]陈和清. 基于汽车高强度板的冲压回弹基础研究[D]. 重庆:重庆大学, 2008.Chen heqing. Basic Research on Stamping Springback of Automobile High Strength Sheet Metal[D]. Chongqing:Chongqing Institute of Technology, 2008.
[10]Cedric Z,Raig X, Miller E, et al. A Bench-mark test for springback experimental procedure sand results of a slit-ring test[J].SAE Technical Paper Series, 2005, 83(1): 1-8.


 

服务与反馈:
本网站尚未开通全文下载服务】【加入收藏
《锻压技术》编辑部版权所有

中国机械工业联合会主管 北京机电研究所有限公司 中国机械工程学会塑性工程分会主办
联系地址:北京市海淀区学清路18号 邮编:100083
电话:+86-010-62920652 +86-010-82415085 传真:+86-010-62920652
E-mail: fst@263.net(稿件) dyjsjournal@163.com(广告)
京ICP备09032115号-5