大断面收缩率一次楔入轧件心部缺陷的实验研究
英文标题:Experimental study on internal defect of heavy section shrinkage workpiece under one cross wedge rolling
作者:何巍巍 张康生 贾震 胡正寰  
单位:北京科技大学机械工程学院  
关键词:楔横轧  心部缺陷  大断面收缩率  成形角 
分类号:TG335.19
出版年,卷(期):页码:2009,34(2):27-30
摘要:
为深入考察楔横轧大断面收缩率一次楔入轧件的心部质量状况,在H500轧机上进行了不同工艺条件下的轧制实验,得到了断面缩减率大于75%的一次楔成形时轧件心部不易产生宏观缺陷;揭示出各个工艺参数对轧件心部缺陷的影响规律;并发现成形角是影响心部质量的决定性因素,大成形角有减少缺陷产生的趋势。研究结果为进一步探索楔横轧的心部缺陷机理提供了依据。
To further study the state of the internal defects of heavy section shrinkage workpiece under one cross wedge rolling,the rolling experiment under different process conditions was done on H500 rolling mill.It is found that when the cross section shrinkage of one cross wedge rolling workpiece is bigger than 75%,the rolled pieces are not easy to have macroscopic internal defects.The influence rules of processing parameters to the internal defects are discovered and the forming angle is the most important mechanical parameter to affect the internal defects.The big forming angle has a tendency to reduce the internal defects.The results provide a guideline for the internal defect formation mechanism.
基金项目:
国家自然科学基金项目(50575023,50435010);; 高等学校博士学科点专项科研基金项目(20050008024);; 国家科技支持计划项目(2006BAF04B03)
作者简介:
参考文献:
[1]娄依志,张康生,胡正寰.工艺参数对楔横轧二次楔入极限断面收缩率的影响[J].北京科技大学学报,2008,30(4):432-435.
[2]潘必刚.楔横轧轧件疏松机理研究[D].北京:北京科技大学,1983.
[3]蔡亚宁,张康生,娄依志,等.成形角对楔横轧大断面收缩率二次楔陷的影响[J].锻压技术,2008,33(3):68-71.
[4]胡正寰,张康生,王宝雨,等.楔横轧零件成形技术与模拟仿真[M].北京:冶金工业出版社,2005.
[5]张承鉴,张庆生,崔世强,等.楔横轧译文集[M].长春:吉林工业大学锻造工艺研究所,1982.
[6]胡正寰,张康生,王宝雨,等.楔横轧理论与应用[M].北京:冶金工业出版社,1996.
[7]陈素莹,张康生,杨翠萍,等.楔横轧工艺参数对心部疏松的影响[J].锻压技术,2006,31(4):38-40.
[8]张康生,王宝雨,刘晋平,等.楔横轧空心件壁厚变化规律实验研究[J].锻压技术,2000,25(2):34-36.
服务与反馈:
本网站尚未开通全文下载服务】【加入收藏
《锻压技术》编辑部版权所有

中国机械工业联合会主管 北京机电研究所有限公司 中国机械工程学会塑性工程分会主办
联系地址:北京市海淀区学清路18号 邮编:100083
电话:+86-010-82415085 传真:+86-010-62920652
E-mail: fst@263.net(稿件) dyjsjournal@163.com(广告)
京ICP备07007000号-9