摘要：
|
|
提出一种新的复合组织制备工艺方法,即首先通过对板坯采取滚珠滚压的方法来实现其表面塑性变形,随后对板坯进行再结晶退火细化表面微观组织。采用有限元法对Q235坯料的滚珠滚压工艺进行数值模拟,得出了表面应变的分布规律,并且对滚压后及再结晶退火后的金相组织进行了观察。结果表明:滚珠滚压工艺能够实现板坯的表面塑性变形,辅以后继的再结晶退火工艺可以获得表面细晶组织和心部粗晶组织的复合组织。
|
|
A new technique was presented,which was able to localize the plastic deformation on the surface of the billet and refine the surface grains after recrystallization annealing through the ball milling.FEM was employed to simulate the process on the surface of Q235 billet and obtain the strain regularity,which proved that the ball milling could realize the surface plastic deformation.The metallography after the ball milling and the recrystallization annealing were also observed.The results indicate that the ball milling will realize the surface plastic deformation and the compound microstructures that are fine grains on the surface and the coarse grains in the center after the recrystallization annealing are obtained.
|
|
基金项目：
|
|
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]Liu C T,Schneibel J H,Maziasz P J,et al.Tensile proper-ties and fracture toughness of TiAl alloys with controlled mi-crostructures[J].Intermetallics,1996,4(6):429-440.
[2]Klocke F,Lier J.Roller burnishing of hard turned surfaces[J].International Journal of Machine Tools&Manufacture,1998,38(5):419-423.
[3]Luo H,Wang L,Zhang C.Study on the aluminum alloyburnishing processing and the existence of the outstrippingphenomenon[J].Journal of Materials Processing Technolo-gy,2001,116(1):88-90.
[4]Hassan A M.Effects of ball and roller burnishing on the sur-face roughness and hardness of some non-ferrous metals[J].Journal of Materials Processing Technology,1997,72(3):385-391.
[5]Yu X,Wang L.Effect of various parameters on the surfaceroughness of an aluminum alloy burnished with a sphericalsurfaced polycrystalline diamond tool[J].International Jour-nal of Machine Tools&Manufacture,1999,39:459-469.
[6]Némat M,Lyons A C.An investigation of the surface topog-raphy of ball burnished mild steel and aluminum[J].Interna-tional Journal of Advanced Manufacturing Technology,2000,16(7):469-473.
[7]Hassan A M,Al-Jalil H F,Ebied A A.Burnishing force,number of ball passes for the optimum surface finish of brasscomponents[J].Journal of Materials Processing Technology,1998,83(1-3):176-179.
[8]Wagner K,V lkl R,Engel U.Tool life enhancement in coldforging by locally optimized surfaces[J].Journal of MaterialsProcessing Technology,2008,201(1-3):2-8.
|
|
服务与反馈：
|
|
【本网站尚未开通全文下载服务】【加入收藏】
|
|
|
|